Abstract:Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured macrostructure consisting of elongated polycrystalline MgB2 fibers separated by elongated pores. The superconducting Tc, Jc and Fp were correlated with the macrostructure and grain size. Grain size increased with HT time at both 600C and 700C. Jc and hence Fp decreased monotonically but not linearly with grain size. Overall, it was observed that at 700C, the MgB2 reaction was more or less complete after as little as 30 min; at 600C, full reaction completion did not occur until 71 h. into the HT. Transport, Jct(B) was measured in a perpendicular applied field, and the magnetic critical current densities, Jcm\bot(B) and Jcm{\phi}(B), were measured in perpendicular and parallel (axial) applied fields, respectively. Particularly noticeable was the premature dropoff of Jcm\bot(B) at fields well below the irreversibility field of Jct(B). This effect is attributed to the fibrous macrostructure and its accompanying anisotropic connectivity. Magnetic measurements with the field directed along the strand axis yielded a critical density, Jcm\bot(B), for current flowing transversely to the strand axis that was less than and dropped off more rapidly than Jct(B). In the conventional magnetic measurement, the loop currents that support the magnetization are restricted by the lower of Jct(B) and Jcm{\phi} (B). In the present case the latter, leading to the premature dropoff of the measured Jcm(B) compared to Jct(B) with increasing field. This result is supported by Kramer plots of the Jcm{\phi} (B) and Jct(B) data which lead to an irreversibility field for transverse current that is very much less than the usual transport-measured longitudinal one, Birr,t.

Enhancement of the Superconducting Transition Temperature of MgB2 by a Strain-Induced Bond-Stretching Mode Softening.

Biaxial Strain Engineering on the Superconducting Properties of MgB2 Monolayer

Enhancement of superconducting transition temperature in MgB 2 by strain-induced bond-stretching mode softening

Biaxial strain engineering on the superconducting properties of MgB2 thin film

Study on the relationship between uniaxial strain and critical transition temperature of MgB2based on first-principles

Study on the most effective pressure application method to increase the critical temperature of MgB2

Strain effect in MgB2/stainless steel superconducting tape

Possible superlattice formation in high-temperature treated carbonaceous MgB2 at elevated pressure

Biaxial strain tuned electronic structure, lattice thermal conductivity and thermoelectric properties of MgI2 monolayer

Superconductive MgB2 Intercalated Muscovite with Dynamically Tunable Stress

Large Anisotropic Thermal Expansion Anomaly near the Superconducting Transition Temperature in MgB2

Drawing induced texture and the evolution of superconductive properties with heat treatment time in powder-in-tube in-situ processed MgB2 strands

Evolution of multi-gap superconductivity in the atomically thin limit: Strain-enhanced three-gap superconductivity in monolayer MgB$_2$

Suppression of Superconductivity in Epitaxial MgB2 Ultrathin Films

Band Structure of Mgb2 with Different Lattice Constants

Strain Effect On The Superconductivity In Borophenes

Superconductive MgB 2 Intercalated Muscovite with Dynamically Tunable Stress

Atomic-scale mechanism of enhanced electron-phonon coupling at the interface of MgB$_2$ thin film

Fabrication of superconducting magnesium diboride thin films by electron beam annealing

Growth and Anisotropic Transport Properties of Off-Axis MgB2 Thin Films

Properties of MgB 2 Films Fabricated under Different Conditions by Ex-Situ Annealing of Mg/B Multilayer Precursor