Abstract:Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured macrostructure consisting of elongated polycrystalline MgB2 fibers separated by elongated pores. The superconducting Tc, Jc and Fp were correlated with the macrostructure and grain size. Grain size increased with HT time at both 600C and 700C. Jc and hence Fp decreased monotonically but not linearly with grain size. Overall, it was observed that at 700C, the MgB2 reaction was more or less complete after as little as 30 min; at 600C, full reaction completion did not occur until 71 h. into the HT. Transport, Jct(B) was measured in a perpendicular applied field, and the magnetic critical current densities, Jcm\bot(B) and Jcm{\phi}(B), were measured in perpendicular and parallel (axial) applied fields, respectively. Particularly noticeable was the premature dropoff of Jcm\bot(B) at fields well below the irreversibility field of Jct(B). This effect is attributed to the fibrous macrostructure and its accompanying anisotropic connectivity. Magnetic measurements with the field directed along the strand axis yielded a critical density, Jcm\bot(B), for current flowing transversely to the strand axis that was less than and dropped off more rapidly than Jct(B). In the conventional magnetic measurement, the loop currents that support the magnetization are restricted by the lower of Jct(B) and Jcm{\phi} (B). In the present case the latter, leading to the premature dropoff of the measured Jcm(B) compared to Jct(B) with increasing field. This result is supported by Kramer plots of the Jcm{\phi} (B) and Jct(B) data which lead to an irreversibility field for transverse current that is very much less than the usual transport-measured longitudinal one, Birr,t.

Strain effect in MgB2/stainless steel superconducting tape

Biaxial Strain Engineering on the Superconducting Properties of MgB2 Monolayer

Biaxial strain engineering on the superconducting properties of MgB2 thin film

Enhancement of the Superconducting Transition Temperature of MgB2 by a Strain-Induced Bond-Stretching Mode Softening.

Influence of Torsional Strain on the Bi-2212 Tapes and Round Wires under Background Field

High transport critical current density obtained for Powder-In-Tube-processed MgB2 tapes and wires using stainless steel and Cu-Ni tubes

Effect of SiC-Impurity Layer and Growth Temperature on MgB2 Superconducting Tapes Fabricated by HPCVD

Large transport critical currents in unsintered MgB2 superconducting tapes

MgB2 coated superconducting tapes with high critical current densities fabricated by hybrid physical-chemical vapor deposition

Progress in Depositing MgB2 Films on Stainless Steel Substrate

Effect Of Nanoscale C And Sic Doping On The Superconducting Properties Of Mgb2 Tapes

Drawing induced texture and the evolution of superconductive properties with heat treatment time in powder-in-tube in-situ processed MgB2 strands

Superconducting properties of MgB2 wires and tapes with different metal sheaths

MgB 2 thick films with remarkable ductility on stainless steel substrate

Mechanical properties of reinforced MgB2 wires

Influence of mechanical reinforcement of MgB2 wires on the superconducting properties

Preparation and Superconductivity of a MgB2 Superconducting Tape

The strain effect on critical current in YBCO coated conductors with different stabilizing layers

The Effect of Zrsi2 and Sic Doping on the Microstructure and J(C)-B Properties of Pit Processed Mgb2 Tapes

Observation of reversible critical current performance under large compressive strain in Sr0.6K0.4Fe2As2 tapes

Strong influence of precursor powder on the critical current density of Fe-sheathed MgB2 tapes