Abstract:Wear performance and mechanisms of PCBN tools with different CBN content (80% vol. and 95% vol.) and cutting edge geometry (honed edge radius, 0.05 mm chamfered edge width, and 0.10 mm chamfered edge width) in boring powder metallurgy (PM) steels had been evaluated. Post-cutting examination of the worn cutting inserts was performed using focus variation microscopy (FVM), scanning electron microscopy (SEM), and energy dispersive spectrometer (EDS). The advanced three-dimensional wear characterization parameters WRM, WMD, WAM, WMH, and WAA are used to measure the wear of PCBN tools. A novel characterization method of removed material (η1 = WMD/WRM) and adhered material (η2 = WMH/WAM) was used to measure the trend of tool wear in this paper. With the increasing of CBN content, the PCBN tool wear parameters WRM, WMD, and WAA were decreased; adhesion was increased by WAM and WMH parameter characterization. For the variation of cutting edge geometry, chamfered edge showed a higher tool life and better wear performance than honed edge radius. With the increasing of chamfered edge width from 0.05 to 0.10 mm, the three-dimensional wear WRM, WMD, WAM, and WMH were increased. WAA showed an opposite trend and parameters η1 and η2 showed a not convergence trend. Besides typical wear mechanisms such as diffusion, adhesion, abrasive, microchipping was observed on PCBN tool; the tool protection layer (TPL) formation and peeling and impact load could be the reasons to explain the microchipping that occurred on cutting edge. Tool life is measured by surface roughness and calculated according to the number of workpieces processed. The results showed that PCBN tool with 95% vol. CBN content and 0.10 mm chamfered edge width achieves higher tool life.

Experimental Study on Influence of Cutting Speed in High Speed Turning with PCBN Tools

Influence of Tool Geometrical Parameters on High Speed Cutting of Titanium Alloy Ti6Al4V

Experimental Study on Cutting Force and Tool Wear of PCBN Tools in High-speed Turning Nickel-based Superalloy

Research on PCBN Tool Dry Cutting GCr15

Cutting Performance and Wear/Damage Characteristics of PCBN Tool in Hard Milling

Study on 3D topography of machined surface in high-speed hard cutting with PCBN tool

Experimental Investigation on the Machinability of PCBN Chamfered Tool in Dry Turning of Gray Cast Iron

Effect of PCBN tool grade and cutting type on hard turning of high-chromium white cast iron

Wear performance and mechanisms of PCBN tools in boring of powder metallurgy steels

Investigation on Cutting Performance of Micro-Textured Cutting Tools

Experimental Study on High-Speed Turning of Free-Cutting Steel AISI 12L14 Using Multi-Layer Coated Carbide Tools

Tool wear characteristics analysis of cBN cutting tools in high-speed turning of Inconel 718

Experimental Investigation on the Surface Integrity of Hard Machined Components by Super-finish Turning

Performance and wear mechanisms of coated PCBN tools in high-speed turning superalloy GH4202

High Speed Cutting of Inconel 718 with Coated Carbide and Ceramic Inserts

Experimental research on the welding strength of PCBN and cemented carbide materials for cutting tools application

Research on cutting parameters of low-temperature liquid CO 2 assisted PCD tool turning bearing ring

Cutting performance of cubic boron nitride-coated tools in dry turning of hardened ductile iron

High Speed Machining of Hardened AISI 1045 Steel

Experimental Investigation of Surface Integrity in Finish Dry Hard Turning of Hardened Tool Steel at Different Hardness Levels

3D Finite Element Simulation on High-speed Dry Hard Turning Process and Experiment Analysis