EIS Study on Corrosion Process of Anodized Film on AZ91D Magnesium Alloy

Qian Jiangang,Li Di,Wang Chun,Baolan Guo

DOI: https://doi.org/10.3321/j.issn:1002-185x.2006.08.026

2006-01-01

Rare Metal Materials and Engineering

Abstract:Corrosion process of the anodized film on AZ91D magnesium alloy's surface in 3.5% NaCl aqueous solution was investigated with electrochemical impedance spectroscopy (EIS). According to the characteristic of EIS in the corrosion process, the EIS of anodized film at the initiation stage and at the propagation stage of pitting corrosion were simulated using the equivalent circuit of R(RQ)(RQ) and R(Q(R(RQ))) models, respectively. The results show that the solution resistance R-sol and the Y-p of porous layer increased, and the resistance R-p of porous layer and the resistance R-b of dense layer decreased gradually. The n(p) value almost unchanged and the Y-b and n(b) of dense layer have no obvious regularity with prolonged of immersion time at the initiation stage of pitting corrosion. The solution resistance R-sol, the n(1) value and the reaction resistance R-2 in corrosion pit decreased, while the Y-1 increased, the solution resistance R-1, the Y-2 and n(2) of metal/medium interface for the anode in corrosion pit have no substantial regularity with prolonging the immersion time at the propagation stage of pitting corrosion.