Highly Flame Retardant Expanded Polystyrene Foams from Phosphorus–Nitrogen–Silicon Synergistic Adhesives
Zong-Min Zhu,Ying-Jun Xu,Wang Liao,Shimei Xu,Yu-Zhong Wang
DOI: https://doi.org/10.1021/acs.iecr.6b05065
2017-01-01
Industrial & Engineering Chemistry Research
Abstract:Three novel, environmentally friendly, flame-retardant adhesives (FRAs), i.e., (1) poly-N-beta-(aminoethyl)-gamma-aminopropyltrimethoxysilane [P(NTMS)], (2) P(NTMS-phosphoric acid) [P(NTMS-PA)], and (3) P(NTMS-phosphorous acid) [P(NTMS-POA)], are synthesized via a versatile sol gel method. The chemical structures are characterized by FTIR and H-1 NMR. The thermal stabilities of the FRAs are revealed by thermogravimetric analysis (TGA) and they exhibit single; double, and triple degradation processes, respectively. Flame-retardant expanded polystyrene foams (EPSFs) are prepared with these novel environmentally friendly FRAs by a simple coating method, and their flammability is investigated by limiting oxygen index (LOI), UL-94 vertical burning test, and cone calorimeter (CC). With as high as 57 wt % of P(NTMS) coating, the foam gains no rating in the UL-94 test. In contrast, EPSF with 57 wt % of P(NTMS-PA) coating passes the UL-94 V-0 grade with a LOI of 31%, and the foam with only 40 wt % of P(NTMS-POA) also passes the UL-94 V-0 grade with a LOT of 26.5%. CC results demonstrate that 40 wt % of P(NTMS-PA) coating reduced the peak heat release rate (PHRR) of EPSF by 62.1% and increased the residue from 0 to 36.2%. For P(NTMS-POA), the corresponding values are 68.8% and 34.0%, respectively. The morphology of the residues was revealed by SEM, and the corresponding chemical compositions and carbonaceous structure were studied by FTIR, EDX, and Raman spectra. These results indicated a synergy in charring among phosphorus, nitrogen, and silicon, and the resulting protective layers were responsible for the higher fire safety.