Abstract:Intumescent flame retardants (IFR) with phosphorus (P)/nitrogen (N)-containing diphenols (DH, DV and DS) were synthesized from p-hydroxybenzaldehyde (H), vanillin (V) and syringaldehyde (S) with different methoxyl groups on its aromatic ring. The FTIR, 1H NMR, 13C NMR, XPS methods were used to characterize the structures of IFR, and LOI, CCT, SEM, TG methods were used to investigate the flame retardancy and thermal stability of rigid polyurethane (RPU) foams when the three IFR were incorporated into RPU foams. Compared with H, V and S, the DH, DV and DS FTIR spectra showed absorption peaks at 3450 cm−1, 1160 cm−1, and 1222 cm−1, 1050 cm−1 and 740 cm−1, respectively, which attributed to NH, CN, and P = O, P-O, P-C groups. The 1H NMR spectra of DH, DV and DS showed proton signals at 4.8 and 6.0 ppm, which were corresponding to H1 and H2 of CN groups, and corresponding C1 signal appeared around 62.3 ppm in the 13C NMR spectra. The XPS spectra of DH, DV, DS showed peaks at 285, 398 eV and 133.5, 532 eV, which may be due to corresponding C1s, N1s of CN groups and P2p and O1s of P-O-C groups, respectively. These results indicated that the target compounds P/N-containing diphenols DH, DV and DS were synthesized successfully. Flame retardancy index (FRI) values of RPU-DH, RPU-DV, and RPU-DS were 2.33, 2.30 and 2.43, respectively, suggesting that DH, DV, and DS were good flame retardant additives. The THR and HRR values of RPU-DH, RPU-DV, RPU-DS foams were much lower than that of RPU foam. The fire growth rate (FIGRA) of RPU-DH, RPU-DV, and RPU-DS was 29.4%, 30.3%, and 24.4% lower comparing to RPU foam. The LOI value of RPU foam was 19%, while LOI values of RPU-DH, RPU-DV and RPU-DS foams increased to around 26%. These results suggested that the flame retardancy of RPU foams were improved by incorporating DH, DV, and DS. Compared with RPU foam, the CY600 of RPU-DH, RPU-DV and RPU-DS foams increased by 215.2%, 152.2% and 195.6%, respectively, and the char residue after CCT were much compact and homogeneous, which could reduce heat and mass transfer, protecting underlying materials from further combustion in a fire. In conclusion, the P/N-containing diphenols DH, DV and DS were synthesized successfully, and they were good flame retardant additives. The char residue of RPU-DH, RPU-DV and RPU-DS foams increased remarkably, and formed compact and homogeneous char layer. The flame retardancy and thermal stability of RPU-DH, RPU-DV, RPU-DS foams were improved by incorporating DH, DV, and DS.

Synthesis of novel nitrogen‐phosphorus flame retardants and their flameproof to flammable polymers

Synthesis of Polymeric Flame Retardants Containing Phosphorus‐nitrogen‐bromide and Their Application in Acrylonitrile‐butadiene‐styrene

Novel Nitrogen–Phosphorus Flame Retardant Based on Phosphonamidate: Thermal Stability and Flame Retardancy

Synthesis of A Novel Phosphorus–Nitrogen-Silicon Polymeric Flame Retardant and Its Application in Poly(lactic Acid)

Synthesis of Novel Phosphorus-Based Flame Retardants Containing 9,9-Bis (4-Hydroxyphenyl) Fluorine and Their Reinforcements on the Fire Safety of Polypropylene

A Phosphorus-Nitrogen Containing Dendrimer Reduces The Flammability Of Nanostructured Polymers With Embedded Self-Assembled Gel Networks

Synthesis, Flame Retardancy, and Thermal Degradation Behaviors of Novel Organo-Phosphorus Compounds Derived from 9,10-Dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO)

A Novel Flame Retardant Containing Phosphorus, Nitrogen, and Sulfur

Flame retardancies of novel organo-phosphorus flame retardants based on DOPO derivatives when applied to ABS

Facile synthesis of a novel transparent hyperbranched phosphorous/nitrogen-containing flame retardant and its application in reducing the fire hazard of epoxy resin.

SYNTHESIS OF NOVEL FLAME-RETARDANT CONTAINING PHOSPHORUS AND SILICON AND ITS FLAME-RETARDANT EFFECT ON PC/ABS

The effect of the presence of a macromolecular organophosphorus flame retardant, poly(N‐[3‐oxopropylmethylphosphinate]ethyleneimine), on the flammability, thermal stability, and mechanical properties of polyamides

Preparation of a novel phosphorus‐nitrogen containing flame retardant by supramolecular reaction and its application in epoxy resin

Synthesis and Thermal Stability of a Novel Phosphorus-Nitrogen Containing Intumescent Flame Retardant

Eco-friendly Synthesis of Novel Phosphorus Flame Retardants for Multiple Purposes

Synthesis of Three Novel Phosphorus-Containing Flame Retardants and Their Application in Epoxy Resins

A novel polymeric intumescent flame retardant: Synthesis, thermal degradation mechanism and application in ABS copolymer

Synthesis and Characterization of Novel Phosphorous-Silicone-Nitrogen Flame Retardant and Evaluation of Its Flame Retardancy for Epoxy Thermosets

Flame Retardant and Mechanical Properties of a Novel P-containing High Temperature Nylon Composites

Synthesis of phosphorus/nitrogen containing intumescent flame retardants from p-hydroxybenzaldehyde, vanillin and syringaldehyde for rigid polyurethane foams

Synthesis of Novel Intumescing Flame Retardant and Its Application in Polyurethane