Abstract:A high soluble and stable epsilon-Zn(OH)(2) precursor is synthesized at below room temperature to efficiently prepare ZnO whiskers. The experimental results indicate that the formation of ZnO whiskers is carried out mainly via two steps: the formation of ZnO seeds from epsilon-Zn(OH)(2) via the in situ solid conversion, and the following growth of whiskers via dissolution-precipitation route. The decrease of temperature from 25 to 5 degree celsius promotes the formation of epsilon-Zn(OH)(2) with higher solubility and stability, which balances the conversion and dissolution rates of precursor. The Rietveld refinement, DFT calculations and MD simulations reveal that the primary reason for these characteristics is the expansion of e-Zn(OH)(2) lattice due to temperature, causing difficulties in the dehydration of adjacent OH. Simultaneously, the larger specific surface area favors the dissolution of epsilon-Zn(OH)(2). Based on this precursor, well-dispersed ZnO whiskers with 9.82 mu m in length, 242.38 nm in diameter, and an average aspect ratio of 41 are successfully synthesized through a SDSN-assisted hydrothermal process at 80 degree celsius. The process has an extremely high solid content of 2.5% (mass ratio of ZnO to solution) and an overall yield of 92%, which offers a new approach for the scaled synthesis of high aspect ratio ZnO whiskers by liquid-phase method.

Evaporation Growth of Multipod ZnO Whiskers Assisted by a Cu2+ Etching Technique

Growth of hex-pod-like Cu2O whisker under hydrothermal conditions

A Low-Temperature Synthesis of Multiwhisker-Based Zinc Oxide Micron Crystals

Preparation and Growth Mechanism of ZnO Whisker

Preparation and Growth Mechanism of ZnO with Spindle Shape

Synthesis of Uniform Rod-Like, Multi-Pod-Like Zno Whiskers and Their Photo Luminescence Properties

Low-temperature growth of uniform ZnO particles with controllable ellipsoidal morphologies and characteristic luminescence patterns.

Preparation of Well-Aligned ZnO Whiskers on Glass Substrate by Atmospheric MOCVD

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

Double Disks Shaped ZnO Microstructures Synthesized by One-Step CTAB Assisted Hydrothermal Methods

Synthesis of ZnO Whiskers Via Hydrothermal Decomposition Route

In-Situ Growth of ZnO Whiskers on Ti2ZnC MAX Phases

Synthesis and Mechanism of 1D ZnO Based on Alkaline Dissolution‐Conversion Strategy of High Stable and Soluble Ɛ‐zn(oh)2

Preparation of Zno Cluster and Rod-Like Whiskers Through Hydrothermal Methods

Structure-Direct Assembly of Hexagonal Pencil-Like Zno Group Whiskers

A Study on the In-Situ Growth of Highly Oriented Zno Whisker

Large Scale Fabrication Of Periodical Bowl-Like Micropatterns Of Single Crystal Zno

Structure-directing self-organized, one-dimensional ZnO single-crystal whiskers

Synthesis of ZnO whiskers via EDTA-assisted hydrothermal routes

Preparation and Characterization of Monoclinic Rod-Shaped ZrO 2 Whiskers Via Sulfate Flux

Multipod ZnO 3D microstructures