Abstract:A high soluble and stable epsilon-Zn(OH)(2) precursor is synthesized at below room temperature to efficiently prepare ZnO whiskers. The experimental results indicate that the formation of ZnO whiskers is carried out mainly via two steps: the formation of ZnO seeds from epsilon-Zn(OH)(2) via the in situ solid conversion, and the following growth of whiskers via dissolution-precipitation route. The decrease of temperature from 25 to 5 degree celsius promotes the formation of epsilon-Zn(OH)(2) with higher solubility and stability, which balances the conversion and dissolution rates of precursor. The Rietveld refinement, DFT calculations and MD simulations reveal that the primary reason for these characteristics is the expansion of e-Zn(OH)(2) lattice due to temperature, causing difficulties in the dehydration of adjacent OH. Simultaneously, the larger specific surface area favors the dissolution of epsilon-Zn(OH)(2). Based on this precursor, well-dispersed ZnO whiskers with 9.82 mu m in length, 242.38 nm in diameter, and an average aspect ratio of 41 are successfully synthesized through a SDSN-assisted hydrothermal process at 80 degree celsius. The process has an extremely high solid content of 2.5% (mass ratio of ZnO to solution) and an overall yield of 92%, which offers a new approach for the scaled synthesis of high aspect ratio ZnO whiskers by liquid-phase method.

Synthesis of ZnO whiskers via EDTA-assisted hydrothermal routes

Synthesis of ZnO Whiskers Via Hydrothermal Decomposition Route

Hydrothermal Synthesis of ZnO Whiskers from Ɛ-Zn(oh)2 in NaOH/Na2SO4 Solution

Preparation of ZrO 2 whiskers through high pressure and high temperature method

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Synthesis and Mechanism of 1D ZnO Based on Alkaline Dissolution‐Conversion Strategy of High Stable and Soluble Ɛ‐zn(oh)2

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Preparation of Zno Cluster and Rod-Like Whiskers Through Hydrothermal Methods

Structure-directing self-organized, one-dimensional ZnO single-crystal whiskers

Controlled Synthesis of 1D ZnO Nanostructures Via Hydrothermal Process

PEG Assisted Hydrothermal Synthesis of ZnO Nanorods

Hydrothermal Synthesis and Characterization of Uniform Α-Feooh Nanowires in High Yield

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Hydrothermal formation of magnesium oxysulfate whiskers in the presence of ethylenediaminetetraacetic acid

Fe3o4 Nano-Whiskers by Ultrasonic-Aided Reduction in Concentrated Naoh Solution

Progress in hydrothermal formation of dispersive nanoparticles and whiskers

Formation and mechanism of ZnS nanowhiskers via solvothermal route

Fabrication and Morphology of ZnO Nanorods Array Prepared from Aqueous Solution under an Assisted Electrical Field

A Novel Low-Temperature Chemical Solution Route for Straight and Dendrite-Like Zno Nanostructures

Effects of NaOH on Formation of ZnO Nanorods from Ε-Zn(oh)2