Abstract:ZnO nanorods were grown on ITO substrates with different concentration of electrolyte by electrodeposition method. Microstructure, surface topography, photoluminescence Spectra, Raman spectra and water contact angle of the thin films were measured. The XRD results show all samples are hexagonal wurtzite and the intensity of diffraction peaks at (002) preferred orientation are strengthen as electrolyte concentration increase from 0.005 to 0.03 M. As the concentration increases, the average diameter, density and inclination of the ZnO nanorods increased. Room temperature photoluminescence spectras of the ZnO nanorods show a narrow UV band centering at about 377 nm and broad visible emissions around 600 nm and the UV peak intensity revealed a remarkable decreased. Raman spectras exhibit three peaks which are located at 439 cm(-1), 562 cm(-1) and 1095 cm(-1). All samples change from hydrophobicity to hydrophilic after one hour ultraviolet (UV) irradiation. (C) The Author(s) 2015. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution Non-Commercial No Derivatives 4.0 License (CC BY-NC-ND, http://creativecommons.org/licenses/by-nc-nd/4.0/), which permits non-commercial reuse, distribution, and reproduction in any medium, provided the original work is not changed in any way and is properly cited. For permission for commercial reuse, please email: oa@electrochem.org. All rights reserved.

Effects of NaOH on Formation of ZnO Nanorods from Ε-Zn(oh)2

Effect of ammonia on morphology, wettability and photoresponse of ZnO nanorods grown by hydrothermal method

Effects of Electrodeposition Electrolyte Concentration on Microstructure, Optical Properties and Wettability of ZnO Nanorods

Influence of Sodium Dodecyl Sulfonate on the Formation of ZnO Nanorods Fromε-Zn(oh)2

Formation of ZnO Rods with Varying Diameters from Ε-Zn(oh)2

Effect of Electrodeposition Time on Microstructure, Wettability and Optical Properties of ZnO Nanorod Arrays

Effect of Na Concentrations on Microstructure and Optical Properties of Zno Films

Effect of alkali metal hydroxide on formation processes of zinc oxide crystallites from aqueous solutions containing Zn(OH)42? ions

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

PEG Assisted Hydrothermal Synthesis of ZnO Nanorods

Effect of NaOH Concentration on Formation of Ba4Ti13O30 and BaTi5O11 Nanocrystals Prepared by Hydrothermal Method

[The Study on the Growth Process of ZnO Nanorods].

Hydrothermal Synthesis of ZnO Whiskers from Ɛ-Zn(oh)2 in NaOH/Na2SO4 Solution

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

Controlled Synthesis of 1D ZnO Nanostructures Via Hydrothermal Process

Growth of flower-like ZnO on ZnO nanorod arrays created on zinc substrate through low-temperature hydrothermal synthesis

Influence of the mixing ways of reactants on ZnO morphology

Surface Morphology and Optical Properties of Na-doped ZnO Thin Films

Effects of preparing conditions on the electrodeposition of well-aligned ZnO nanorod arrays