Preparation of Polyether Triol and Three-Armed Polyether Triol by Tetrahydrofuran Polymerization Initiated with Heteropolyacid

Y Chen,GL Zhang,HZ Zhang

DOI: https://doi.org/10.1002/1521-3935(20010501)202:8<1440::aid-macp1440>3.0.co;2-r

IF: 2.996

2001-01-01

Macromolecular Chemistry and Physics

Abstract:Polyether triol, containing 74.6–71.9 mol-% oxytetramethylene moieties and 22.9–24.4 mol-% oxyethylene moieties, was prepared in yield around 50% by tetrahydrofuran polymerization using heteropolyacid-ethylene oxide as initiator system and 1,1,1-trihydroxymethylenepropane (TMP) as molecular weight controller. The molecular weight distribution index of product was 1.3–1.5 and the average hydroxyl end-group functionality was determined to be close or equal to 3. The 1H-NMR spectrum showed that about 1/3 hydroxyls of TMP did not react with propagating chains in the polymerization. All the hydroxyls of polyether triol were primary ones and active enough toward 4,4′-methylene bis (phenyl isocyanate) in the preparation of polyurethane as verified by model experiment. The three-armed polyether triol was prepared by using epichlorohydrin as promoter in stead of ethylene oxide. The remained unreacted hydroxyls of TMP were determined by 1H-NMR to be only 2.1–5.2 mol-%, comparing with 24.5–29.4 mol-% as ethylene oxide promoter was used. The average hydroxyl end-group functionality was close to 3, the polymerization yield was around 80% and molecular weight of the three-armed polyether triol was 3 000–4 000.