Abstract:It is difficult to achieve Al/Cu dissimilar welds with good mechanical properties for medium-thick plates due to the inherent high heat generation rate at the shoulder-workpiece contact interface in conventional friction stir welding. Thus, double-side friction stir welding is innovatively applied to join 12-mm medium-thick 6061-T6 aluminum alloy and pure copper dissimilar plates, and the effect of welding speeds on the joint microstructure and mechanical properties of Al/Cu welds is systematically analyzed. It reveals that a sound Al/Cu joint without macroscopic defects can be achieved when the welding speed is lower than 180 mm/min, while a nonuniform relatively thick intermetallic compound (IMC) layer is formed at the Al/Cu interface, resulting in lots of local microcracks within the first-pass weld under the plunging force of the tool during friction stir welding of the second-pass, and seriously deteriorates the mechanical properties of the joint. With the increase of welding speed to more than 300 mm/min void defects appear in the joint, but the joint properties are still better than the welds performed at low welding speed conditions since a continuous uniform thin IMCs layer is formed at the Al/Cu interface. The maximum tensile strength and elongation of Al/Cu weld are, respectively, 135.11 MPa and 6.06%, which is achieved at the welding speed of 400 mm/min. In addition, due to the influence of welding distortion of the first-pass weld, the second-pass weld is more prone to form void defects than the first-pass weld when the same plunge depth is applied on both sides. The double-side friction stir welding is proved to be a good method for dissimilar welding of medium-thick Al/Cu plates.

Weld Brazing of Copper Thick Plates

Microstructure and Mechanical Performance of Gta Weld Brazed Joints of Copper Thick Plates

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

Dissolution Behavior of Cu in Cu-Ag and Cu-P Brazing Alloys Using Weld Brazing

TIG welding-brazing joints of aluminum-stainless steel with different thickness of base metals

Thermal effects of gas tungsten arc welding for thick copper plates at different welding condition

A Comparative Study of Friction Stir Brazing and Furnace Brazing of Dissimilar Metal Al and Cu Plates

Brazability of dissimilar metals tungsten inert gas butt welding–brazing between aluminum alloy and stainless steel with Al–Cu filler metal

Microstructure and Properties of Dissimilar Butt Joints of Aluminum to Copper by Cold Metal Transfer with Preheating

Microstructure and Mechanical Properties of Dissimilar Double-Side Friction Stir Welds Between Medium-Thick 6061-T6 Aluminum and Pure Copper Plates

Microstructure and Performance of Hybrid Laser-Arc Welded 40 Mm Thick 316 L Steel Plates

Interface Microstructure and Mechanical Property of CMT Welding-Brazed Joint Between Aluminum and Galvanized Steel Sheet

Effect of Ultrasonic Power on Microstructural and Mechanical Properties of Al/Cu Plasma Arc Welding–Brazing Joints

The Dissolution Mechanism of Copper Weld Brazing with Cu-Based Brazing Alloys

Microstructures and Mechanical Behavior of Aluminum-Copper Lap Joints

Microstructure and mechanical properties of Al/Cu dissimilar metals pulsed DE-MIG welding-brazing joint

Brazing Oxide Dispersion-Strengthened Fe-Based Steels with a Cu-Based Filler Metal

Effect of Filler Wires on Brazing Interface Microstructure and Mechanical Properties of Al/Cu Dissimilar Metals Welding-Brazing Joint

Effect of brazing temperature on interfacial microstructure and mechanical property of Ti60/AgCu/ZrO2 joint

Microstructure and Mechanical Properties in Friction Stir Welded 5A06 Aluminum Alloy Thick Plate

Investigation on the interfacial microstructure and mechanical properties of the W-Cu joints fabricated by hot explosive welding