Abstract:Tungsten production primarily relies on scheelite, a secondary resource due to its complex ore composition and lower grade compared to high-grade wolframite. Synthetic scheelite gains significance for its low impurity content and accessibility in ongoing laboratory-based investigations. Recent advancements offer a feasible environment-friendly leaching method using a mixed solution of H 2 SO 4 and H 2 O 2 under normal pressure and moderate temperatures. However, comprehensive research on this novel method is lacking, emphasising the need for collaborative exploration and operational optimisation. The present work is to provide insights and improvements in reagent usage to promote economic and environmental sustainability. A detailed investigation into the thermal decomposition process was also conducted without compromising leaching efficiency. The findings suggest the potential for eco-friendly lixivium recycling with reduced levels of chemicals, decreasing operational costs. Notably, optimising the thermal decomposition duration to 6 hours at an L/S (mL/g) ratio of 10 enhances H 2 WO 4 crystallization. Furthermore, experiments without H 2 SO 4 supplementation highlight the system's optimisation potential. Finally, the leaching process was optimised by decreasing H 2 SO 4 concentration to 1 mol/L from 3 mol/L, increasing the temperature to 60°C, and extending the leaching duration to 120 minutes. This leads to a cost-effective synthetic scheelite leaching process with environmental benefits. La production de tungstène se fie principalement à la scheelite, une ressource secondaire en raison de la composition complexe de son minerai et de sa teneur inférieure par rapport à celle de la wolframite à haute teneur. La scheelite synthétique gagne en importance en raison de sa faible teneur en impuretés et son accessibilité dans les investigations en cours en laboratoire. Des progrès récents offrent une méthode de lixiviation réalisable et écologique utilisant une solution mixte de H 2 SO 4 et de H 2 O 2 sous une pression normale et à des températures modérées. Cependant, il manque des recherches approfondies sur cette nouvelle méthode, mettant l'emphase sur le besoin d'une exploration collaborative et d'une optimisation opérationnelle. Le travail courant vise à fournir des connaissances et des améliorations dans l'utilisation des réactifs pour favoriser la durabilité économique et environnementale. Une investigation détaillée du procédé de décomposition thermique a également été entreprise sans compromettre l'efficacité de la lixiviation. Les résultats suggèrent le potentiel d'un recyclage écologique du lixiviat avec une réduction de niveaux de produits chimiques, diminuant les coûts opérationnels. Notamment, l'optimisation de la durée de décomposition thermique à 6 heures à un rapport L/S (ml/g) de 10 améliore la cristallisation de H 2 WO 4 . De plus, des expériences sans supplémentation en H 2 SO 4 soulignent le potentiel d'optimisation du système. Finalement, on a optimisé le procédé de lixiviation en diminuant la concentration de H 2 SO 4 de 3 mol/L à 1 mol/L, en augmentant la température à 60°C et en étendant la durée de lixiviation à 120 minutes. Cela conduit à un procédé de lixiviation de la scheelite synthétique qui est économique avec des avantages environnementaux.

Hydrothermal Synthesis of Wollastonite from Desilication Filtrate

An Experimental Study on Preparation of Nanocrystalline Wollastonite Powders from Sodium-Calcium Siliceous Hydration Residue

Hydrothermal Synthesis of Acicular Wollastonite from Potassium Silicate Solution

Synthesis of Pure-Silica Mtw Powder and Supported Films

Simple and rapid synthesis of zeolite W from K‐feldspar via the improved hydrothermal method

Preparation of Nano-Sized Wollastonite Using Calcium Silicate Residue of Potassium Feldspar after Extraction of Potassium and Alumina

Preparation of Acicular Wollastonite Using Hydrothermal and Calcining Methods

Preparation of potassium sulfate from K-feldspar by hydrothermal alkaline method:reaction principle and process evaluation

Preparation of potassium sulfate and zeolite NaA from K-feldspar by a novel hydrothermal process

Utilization of industrial waste materials for the preparation of wollastonite by temperature-induced forming technique

Optimization of synthesis parameters for the preparation of zeolite by reusing industrialwaste as raw material: Sandblasting waste and solar panel waste glass

Synthesis of Wollastonite Nanowires Via Hydrothermal Microemulsion Methods

Transformation of Coal Gangue to Sodalite and Faujasite Using Alkali-hydrothermal Method

An optimisation study for leaching synthetic scheelite in H2SO4 and H2O2 solution

A novel method for surface wettability modification of talc through thermal treatment

A novel combined metallurgy-beneficiation method for the facile and low-cost comprehensive resource utilization of low-grade kaolin solid wastes

Preparation of ZSM-5 molecular sieve by diatomaceous earth in-situ crystallization

Hydrothermal Solidification of Siliceous and Calcareous Wastes into Building Materials: A Generic Mix Design Framework

Hydrothermal alkaline synthesis and release properties of silicon compound fertiliser using high-ash coal slime

Hydrothermal synthesis of high crystallinity ZSM-5 zeolite from coal gasification coarse slag and mother liquor circulation for efficient coal chemical wastewater purification

A Feasible Route for Preparation of Calcium Sulfate Whiskers from FGD Gypsum via Filtrate Recycle under Hydro-Thermal Conditions