Abstract:Symmetric hierarchical hollow PbS structures consisting of nanowalls were successfully fabricated by a facile solvothermal process in ethylenediamine at 120 degrees C for 12 h, employing lead acetate trihydrate and dithizone as precursors; the thickness of the nanowalls is about 80 nm. No surfactants or other templates were used in the process. The synthesized product was characterized by X-ray powder diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), ultraviolet-visible spectrometer (UV-vis), near-infrared absorption spectroscopy (near-IR), and fluorescence spectrophotometer. The effect of the reaction conditions on the size and morphologies of PbS structures was investigated. The results show that the temperatures, solvent, and sulfur sources are crucial factors on the morphologies and sizes of the symmetric hierarchical hollow PbS microcrystals. A possible growth mechanism of hierarchical hollow PbS structures is presented. UV-vis absorption spectrum holds a weak peak at 253 nm; the near-infrared absorption spectrum of PbS microcrystals has the two absorption peaks centered at 9613 cm(-1) (1040 nm) and 6771 cm(-1) (1477 nm), showing a blue shift compared with the bulk PbS (approximately 3020 nm). And the fluorescence spectrum of PbS microcrystals consists of an emission peak with a maximum at 305 nm. These PbS microcrystals may have potential applications in the fundamental study of nanostructures as well as fabricating nanodevices.

Nonsurfactant synthesis of PbS crystals via electrodeposition and hydrothermal methods: from octahedron to maya-pyramid

Shape-Controlled Syntheses of Pbs Submicro-/Nano-Crystals Via Hydrothermal Method

Shape Controllable Preparation and Characterization of Hierarchical PbS Submicron Cubes Via a Solvothermal Method

Flowerlike Pbs Microcrystals: Citric Acid Assisted Synthesis, Shape Evolution, and Electrical Conductivities

Shape Controllable Growth of PbS Polyhedral Crystals

Morphology Evolution Route of PbS Crystals Via Environment-Friendly Electrochemical Deposition

Hydrothermal synthesis of PbS hollow spheres with single crystal-like electron diffraction patterns.

Facile Solvothermal Synthesis of Nanostructured Pbse with Anisotropic Shape: Nanocubes, Submicrometer Cubes and Truncated Octahedron

Facile synthesis of PbS truncated octahedron crystals with high symmetry and their large-scale assembly into regular patterns by a simple solution route.

Shape-controlled Synthesis of PbS Microcrystals in Large Yields Via a Solvothermal Process

PbS Cubes with Pyramidal Pits: An Example of Etching Growth

Growth of PbS crystals from nanocubes to eight-horn-shaped dendrites through a complex synthetic route

Synthesis and evolution of PbS nanocrystals through a surfactant-assisted solvothermal route.

Fabrication of Symmetric Hierarchical Hollow PbS Microcrystals Via a Facile Solvothermal Process

Diethylenetriamine-Assisted Hydrothermal Route to Synthesize Cuboidal Structure of PbSe Crystal

Surfactant‐Assisted Growth of Novel PbS Dendritic Nanostructures Via Facile Hydrothermal Process

L-Cysteine-Assisted Synthesis of PbS Nanocube-Based Pagoda-like Hierarchical Architectures

Growth of PbS architectural nanostructures catalyzed by silver nanocrystal seeds

Hydrothermal Synthesis and Morphology Evolution of Perovskite PbTiO<sub>3</sub> Crystals with Different Lead Sources

A novel aqueous-phase route to prepare flower-shaped PbS micron crystals

Surface Synthesis of PbS Nanoparticles on Silica Spheres by a Sonochemical Approach