Abstract:AIM: To improve the mechanical property of poly (3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) and processing ability of polypropylene carbonate (PPC), the PHBHHx and PPC were blended in solvent and made into films and tubular scaffolds. The adhesion of rabbit aorta smooth muscle cell (RaSMC) on the films and the mechanical property of tubular scaffolds were evaluated to select a proper material as scaffold for blood vessel tissue engineering. METHODS: The experiment was conducted in the State Key Laboratory of Biomembrane and Membrane Bioengineering, Department of Biological Sciences and Biotechnology, Tsinghua University from August 2006 to April 2007. ①RaSMCs were incubated on the films from different weight ratios of PHBHHx/PPC blended solution (PHBHHx: PPC= 0∶10, 3∶7, 5∶5, 7∶3, and 10∶0) for 24 hours and the amounts of adhesion on different films were detected by CCK-8 kit. ②Tubular scaffolds were prepared using thermally-induced phase separation (TIPS) and freeze-drying methods, and then they were dipped into their solutions respectively and dried in air. A dried membrane was formed on the surface of scaffolds. The morphology of the scaffolds was observed by scanning electron microscopy (SEM); the porosity and pore diameter of the scaffolds were measured with a mercury porosimeter. Mechanical property including burst pressure and suture retention strength was evaluated by self-made instrument at 6.65 kPa/s and omnipotent material testing machine, respectively. Ovine carotid artery served as control. RESULTS: ①After 24 hours, 5∶5 PHBHHx/PPC and PPC films exhibited better RaSMC affinity than PHBHHx alone (P < 0.05). ②After dipping into solutions, PHBHHx and PHBHHx/PPC scaffolds maintained original tubular form with a film layer outside, while porous PPC scaffold dissolved as dipping into PPC solution and drying in air. The pore diameter enlarged and the porosity augmented with the increase of PPC content in the blended solution. ③Burst pressure of the scaffold was similar to that of ovine carotid artery (P > 0.05), and suture retention strength was superior to that of ovine carotid artery. Moreover, the suture retention strength of PHBHHx/PPC scaffolds at ratio of 5∶5 and 3∶7 was higher than that of PHBHHx scaffold. CONCLUSION: ①Adhesion of RaSMC on 5∶5 PHBHHx/PPC and PPC films is better than PHBHHx film. ②PHBHHx and PHBHHx/PPC blended solution can be prepared into porous tubular scaffold with a film layer outside. The mechanical properties of the scaffolds are appropriate for implantation, especially that of 5∶5 and 3∶7 PHBHHx/PPC scaffolds.

Guided growth of smooth muscle cell on poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) scaffolds with uniaxial microtubular structures.

Fabrication of a tubular vascular scaffold with circumferential microchannels to induce oriented growth of smooth muscle cells

Primary Culture and 3-Dimensional Scaffold Culture of Rat Gastric Smooth Muscle Cells in Vitro

Properties of poly (3-hydroxybutyrate-co-3-hydroxyhexanoate)/poly propylene carbonate blended materials as a scaffold for blood vessel tissue engineering

Effect of 3-hydroxyhexanoate content in poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) on in vitro growth and differentiation of smooth muscle cells.

Tendril Climber Inspired Structure-Induced Cell Growth by Direct Writing Heterogeneous Scaffold

Structure-induced Cell Growth by 3D Printing of Heterogeneous Scaffolds with Ultrafine Fibers

Fabrication of a Dual-Layer Cell-Laden Tubular Scaffold for Nerve Regeneration and Bile Duct Reconstruction.

Decellularized Scaffolds with Double‐Layer Aligned Microchannels Induce the Oriented Growth of Bladder Smooth Muscle Cells: toward Urethral and Ureteral Reconstruction

Growth of human smooth muscle cells on the silk fibroin modified-polyhydroxyalkanoate scaffold

Study on the three-dimensional proliferation of rabbit articular cartilage-derived chondrocytes on polyhydroxyalkanoate scaffolds.

Manufacturing and morphology structure of polylactide-type microtubules orientation-structured scaffolds.

Polyhydroxyalkanoate (PHA) Scaffolds with Good Mechanical Properties and Biocompatibility

Attachment, Proliferation and Differentiation of Osteoblasts on Random Biopolyester Poly(3-Hydroxybutyrate-co-3-hydroxyhexanoate) Scaffolds.

Biomimic Tubulose Scaffolds with Multilayer Prepared by Electrospinning for Tissue Engineering

Additive Manufacturing of Poly[(r)-3-hydroxybutyrate-co-(r)-3-hydroxyhexanoate] Scaffolds for Engineered Bone Development.

Fabrication of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) microstructures using soft lithography for scaffold applications.

Electrospun Biodegradable α-Amino Acid-Substituted Poly(organophosphazene) Fiber Mats for Stem Cell Differentiation towards Vascular Smooth Muscle Cells

A preliminary study on polycaprolactone and gelatin-based bilayered tubular scaffolds with hierarchical pore size constructed from nano and microfibers for vascular tissue engineering

Embryonic Mesenchymal Multipotent Cell Differentiation on Electrospun Biodegradable Poly(ester amide) Scaffolds for Model Vascular Tissue Fabrication

Bi‐Layered Tubular Microfiber Scaffolds as Functional Templates for Engineering Human Intestinal Smooth Muscle Tissue