Properties of poly (3-hydroxybutyrate-co-3-hydroxyhexanoate)/poly propylene carbonate blended materials as a scaffold for blood vessel tissue engineering

L Zhang,Q Ao,Q He,G Wang,J Xi,YD Gong,XF Zhang
DOI: https://doi.org/10.3321/j.issn:1673-8225.2007.35.008
2007-01-01
Abstract:AIM: To improve the mechanical property of poly (3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBHHx) and processing ability of polypropylene carbonate (PPC), the PHBHHx and PPC were blended in solvent and made into films and tubular scaffolds. The adhesion of rabbit aorta smooth muscle cell (RaSMC) on the films and the mechanical property of tubular scaffolds were evaluated to select a proper material as scaffold for blood vessel tissue engineering. METHODS: The experiment was conducted in the State Key Laboratory of Biomembrane and Membrane Bioengineering, Department of Biological Sciences and Biotechnology, Tsinghua University from August 2006 to April 2007. ①RaSMCs were incubated on the films from different weight ratios of PHBHHx/PPC blended solution (PHBHHx: PPC= 0∶10, 3∶7, 5∶5, 7∶3, and 10∶0) for 24 hours and the amounts of adhesion on different films were detected by CCK-8 kit. ②Tubular scaffolds were prepared using thermally-induced phase separation (TIPS) and freeze-drying methods, and then they were dipped into their solutions respectively and dried in air. A dried membrane was formed on the surface of scaffolds. The morphology of the scaffolds was observed by scanning electron microscopy (SEM); the porosity and pore diameter of the scaffolds were measured with a mercury porosimeter. Mechanical property including burst pressure and suture retention strength was evaluated by self-made instrument at 6.65 kPa/s and omnipotent material testing machine, respectively. Ovine carotid artery served as control. RESULTS: ①After 24 hours, 5∶5 PHBHHx/PPC and PPC films exhibited better RaSMC affinity than PHBHHx alone (P < 0.05). ②After dipping into solutions, PHBHHx and PHBHHx/PPC scaffolds maintained original tubular form with a film layer outside, while porous PPC scaffold dissolved as dipping into PPC solution and drying in air. The pore diameter enlarged and the porosity augmented with the increase of PPC content in the blended solution. ③Burst pressure of the scaffold was similar to that of ovine carotid artery (P > 0.05), and suture retention strength was superior to that of ovine carotid artery. Moreover, the suture retention strength of PHBHHx/PPC scaffolds at ratio of 5∶5 and 3∶7 was higher than that of PHBHHx scaffold. CONCLUSION: ①Adhesion of RaSMC on 5∶5 PHBHHx/PPC and PPC films is better than PHBHHx film. ②PHBHHx and PHBHHx/PPC blended solution can be prepared into porous tubular scaffold with a film layer outside. The mechanical properties of the scaffolds are appropriate for implantation, especially that of 5∶5 and 3∶7 PHBHHx/PPC scaffolds.
What problem does this paper attempt to address?