Abstract:ABSTRACTPolyethylene hollow spheres with diameters of 0.4–2 mm were synthesized by a two‐step slurry polymerization in a single reactor with a spherical MgCl2‐supported Ziegler‐Natta catalyst activated by triethylaluminum, in which the first step was prepolymerization with 0.1 MPa propylene and the second step was ethylene polymerization under 0.6 MPa. The prepolymerization step was found necessary for the formation of hollow spherical particles with regular shape (perfectly spherical shape). The effects of adding small amount of propylene (propylene/ethylene < 0.1 mol/mol) in the reactor after the prepolymerization step were investigated. Average size of the polymer particles was increased, and the polymerization rate was markedly enhanced by the added propylene. Development of the particle morphology with polymerization time was also studied. The polymer particles formed by less than 20 min of ethylene polymerization showed hollow spherical morphology with thin shell layer. Most of the particles had ratio of shell thickness/particle radius smaller than 0.5. By prolonging the ethylene polymerization, the shell thickness/particle radius ratio gradually approached 1, and the central void tended to disappear. Central void in polymer particles formed from smaller catalyst particles disappeared after shorter time of polymerization than those formed from bigger catalyst particles. The shell layer of the hollow particles contained large number of macro‐, meso‐ and micro‐pores. The mesopore size distributions of four typical samples were analyzed by nitrogen adsorption–desorption experiments. A simplified multigrain model was proposed to explain the morphogenesis of the hollow spherical particles. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016, 133, 43207.

Controlled Growth of Carbon Spheres Through the Mg-Reduction Route

Self-assembled Flower-Like Hierarchical Spheres and Nanobelts of Manganese Oxide by Hydrothermal Method and Morphology Control of Them

One-step Syntheses and Properties of Carbon Microspheres with Amino Groups

Synthesis of Carbon Hollow Spheres by a Reaction of Hexachlorobutadiene with Sodium Azide

A novel route to hollow and solid carbon spheres

Direct Synthesis Of Uniform Hollow Carbon Spheres By A Self-Asembly Template Approach

Controllable Synthesis, Characterization, and Growth Mechanism of Hollow Znxcd1-Xs Spheres Generated by A One-Step Thermal Evaporation Method

Controlled Synthesis of N-Doped Carbon Spheres with Different Morphologies for Supercapacitors

Large-scale synthesis and characterization of carbon spheres prepared by direct pyrolysis of hydrocarbons

Morphology Control in the Synthesis of Caco3 Microspheres with A Novel Co2-Storage Material

Controlled Synthesis, Growth Mechanism, and Properties of Monodisperse CdS Colloidal Spheres.

Millimeter-Size Polyethylene Hollow Spheres Synthesized with Mgcl2-Supported Ziegler-Natta Catalyst

The Synthesis of a Core–shell Hybrid Composite Micro-Sphere with Controllable Homogenous or Heterogeneous Multi-Shell Structure by Multiple-Growth Via a Combination Method

Self-templated Synthesis of Heavily Nitrogen-Doped Hollow Carbon Spheres

Controllable Synthesis of Hollow Periodic Mesoporous Organosilica Spheres with Radial Mesochannels and Their Degradable Behavior

Preparation of Carbon Micro-Spheres by Hydrothermal Treatment of Methylcellulose Sol

Synthesis of Hollow Mesoporous Silica Spheres with Radially Aligned Mesochannels and Tunable Textural Properties

Synthesis of Submicrometer-Sized Cds Hollow Spheres in Aqueous Solutions of A Triblock Copolymer

Hollow Silica Spheres with an Ordered Pore Structure and Their Application in Controlled Release Studies

A Low-Temperature in Situ Template Reduction-Carbonization Route to Tic Submicrometer Hollow Spheres and Nanorods

Large-scale synthesis of mesoporous carbon microspheres with controllable structure and nitrogen doping using a spray drying method