Abstract:In order to research the effect pattern of MnS inclusions on free-cutting steel, we study the microstructure evolution, the damage mechanism and the mechanical properties in free-cutting steel in the presence of MnS inclusions. Spindle shaped MnS is added as inclusions within the free-cutting steel. The mechanical properties were found to change when inclusions were present. The gained results show that the formation of voids causing fracture starts from the interface inside the matrix close to the MnS. From the point of view of nanocomposite strength, the main effect of MnS inclusions is related to stress concentration, leading to the effect of increased stresses near the interface between the interior of the matrix and the inclusions. The inclusions have lower Young's modulus and lower dislocation activity, resulting in smaller deformation of the alloy system, larger interfacial stress concentrations and earlier hole formation. The maximum strain and stress regions of the alloy also appear near the MnS inclusions, which leads to the formation of defects near the MnS inclusions and then fracture of the alloy. MnS inclusions adversely affect the tensile properties of the alloy, such as Young's modulus, yield stress and yield strain. By comparing the stress-strain curves of single crystal iron and alloy containing MnS inclusions, it is indicated that the yield strength of the latter decreases. Slip bands and dislocation lines are first generated around the MnS inclusion, and the phase transition is induced from the original single BCC structure to FCC, HCP and amorphous structures, and the atoms of FCC, HCP and amorphous structures increase with increasing strain, while those of BCC structure decrease, especially after yield strain. This study is significant for understanding the effect of inclusions on the mechanical laws and fracture mechanisms of the alloy.

Influence of Characteristic Inclusion Parameters on Crack Initiation in Ultra-High Strength Steel Under Tensile Load

Study on Micro-Mechanism of Crack Initiation and Propagation Induced by Inclusion in Ultra-High Strength Steel

Sem in Situ Observations to the Effects of Inclusions on Initiation and Propagation of the Low Cyclic Fatigue Crack in Super Strength Steel

Study on Inclusion Induced Fatigue Crack Initiation and Propagation in Ultra-High Strength Steel for Aerospace Application

Effects of Non-Metallic Inclusions on the Crack Propagation in Bearing Steel

Influence of Non-Metallic Inclusions on Very High-Cycle Fatigue Performance of High-Strength Steels and Interpretation via Crystal Plasticity Finite Element Method

High-Cycle Fatigue Fracture Behavior of Ultrahigh Strength Steels

Cracking in a Fe–25Mn–3Si–3Al Steel

Effects of MnS inclusions on mechanical behavior and damage mechanism of free-cutting steel: A molecular dynamics study

Mechanism for Development of Faults Originating from Compound Inclusions in the Forging Process of 30cr2ni4mov Heavy Ingots

Effect of Inclusions and Microstructural Characteristics on the Mechanical Properties and Fracture Behavior of a High- Strength Low- Alloy Steel

The Effect of Inclusions on the Fatigue Behavior of Fine-Grained High Strength 42crmovnb Steel

Study on the Crack–inclusion Interaction with Coupled Mechanical and Thermal Strains

Non-inclusion induced crack initiation in multiphase high-strength steel during very high cycle fatigue

Study on the plane stress mode II crack–inclusion interaction with coupled mechanical and thermal strains

Characteristics of Fatigue Surface Microcrack Growth in Vicinal Inclusion for Powder Metallurgy Alloys

Effect of Non-metallic Inclusions on the Local Stress Concentration Within Materials

Unveiling the mechanism behind irregular inclusions triggering no HIC cracks in steels

Assessment of microstructure- and inclusion-induced fatigue crack initiation in bainitic/martensitic rail steels: competing and synergistic effects

Influence of Inclusion Morphology on Impact Fracture Behavior in High-Strength Pipeline Steel

The Effect of Inclusions on a Medium Temperature Transformation Microstructure and Toughness of High-Strength HSLA Steel