Synthesis of CMC-Stabilized Fe/Ni Bimetallic Nanoparticles for in situ Reductive Dechlorination of PCB77

ZHAO Lin,DING Shu,TAN Xin,YU Shun-lei
DOI: https://doi.org/10.13353/j.issn.1004.9533.2012.05.005
2012-01-01
Abstract:The CMC-Ni-Fe bimetallic nanoparticles were successful synthesized with the monodispersed carboxymethyl cellulose(CMC) as a stabilizer.The various reaction parameters were optimized.Nanoparticles,prepared with m(CMC)/m(Fe)=5 and m(Ni)/m(Fe)=0.03 at 25 ℃,showed the best degradation effect of PCB77.Near 94% of reduction efficiency was achieved by CMC-Ni/Fe bimetallic nanoparticles for 48 h treatment,while only about 71% PCB77 was degraded by Ni/Fe bimetallic nanoparticles.The results of XRD showed that the CMC-Ni/Fe bimetallic nanoparticles exhibited the characteristic peaks of elemental iron and the characteristic peaks of iron oxides were not detected.It was indicated that the elemental iron of CMC-Ni/Fe bimetallic nanoparticles was not oxidized in preparation process.The results of particle size analysis were demonstrated that the average diameter of CMC-stabilized Ni-Fe bimetallic nanoparticles was about 23.94 nm,smaller than the particle size of Ni/Fe bimetallic nanoparticles(100 nm).
What problem does this paper attempt to address?