Abstract:The influence of phosphate as a corrosion inhibitor on the corrosion behavior of as-received and pre-rusted reinforcing steels in mortar specimens was investigated after 360days exposure in 3.5% NaCl solution. This involved the use of electrochemical techniques for studying the steel surface reactions and microscopic observations of the steel–mortar interface. The electrochemical methods, including electrochemical impedance spectroscopy (EIS) and measurements of corrosion potential (Ecorr) and linear polarization resistance (LPR), were employed to evaluate the corrosion tendency and general corrosion rate of steel. In addition, the pitting corrosion resistance of steel was also determined by cyclic polarization (CP) measurements. The results indicate that different from nitrite, which is generally accepted as an anodic inhibitor, phosphate may be a cathodic inhibitor according to its reduced corrosion rate and more negative Ecorr at the same dosage as nitrite in mortar specimens. The study also reveals that the inhibiting efficiency of phosphate against general corrosion of both as-received and pre-rusted specimens is lower than 10%, which is inferior to nitrite in some respects. However, as indicated by cyclic polarization measurements, the presence of phosphate provides slightly higher pitting corrosion resistance in comparison to nitrite. Furthermore, it suggests that the corrosion inhibition mechanism of phosphate in mortars mainly depends on a dual effect occurring at the steel–mortar interface. Furthermore, it is confirmed that phosphate has little effect on the long-term mechanical properties of mortars.

Effect of Mineral Admixtures and Steel Surface Conditions on Steel Corrosion in Mortar

An Electrochemical and Microstructural Characterization of Steel-Mortar Admixed with Corrosion Inhibitors

INFLUENCE OF MINERAL ADMIXTURES ON CHLORIDE THRESHOLD LEVEL FOR CORROSION OF STEEL IN MORTAR

Corrosion Inhibition Performances at the Steel-Mortar Interface. Part 1: A Surface Analytical Investigation

Effects and Mechanisms of Mineral Admixtures on Sulfate Attack of Cement Mortars

Effects of Corrosion Inhibitor and Mineral Admixtures on Performance of Corrosion Concrete Repairing Mortar

CORROSION BEHAVIOR OF STEEL REINFORCEMENT EMBEDDED IN CEMENT MORTAR WITH SURFACE TREATMENT

Effect of Different Mineral Admixtures on Sulfate Attack to Mortars

Reinforcing Steels in Low-Carbon Mortars Subjected to Chloride Attack and Natural Carbonation: Contradictory Trends in Passivation Ability and Corrosion Resistance

Exploration into Anticorrosive Property of Antirust Compound-Admixture

Long-term Corrosion Resistance of Reinforcing Steel in Alkali-Activated Slag Mortar after Exposure to Marine Environments

Steel Corrosion Behavior of Reinforced Calcium Aluminate Cement-Mineral Additions Modified Mortar

Effects of Phosphate on the Chloride-Induced Corrosion Behavior of Reinforcing Steel in Mortars

Effect of modified supplementary cementitious material on performance of mortar and concrete in marine environment

Corrosion of Steel Embedded in Mortar and Concrete under Different Electrolytic Accelerated Corrosion Methods

Corrosion Behaviour of Low-Carbon Steel Reinforcement in Alkali-Activated Slag-Steel Slag and Portland Cement-Based Mortars under Simulated Marine Environment

Influence of mineral admixtures on corrosion resistance of cement mortar exposed to strong acid and salt composite groundwater

Effects of Sulfate and Magnesium Ion on the Chloride Transportation Behavior and Binding Capacity of Portland Cement Mortar

In-depth Insight into the Role of Molybdate in Corrosion Resistance of Reinforcing Steel in Chloride-Contaminated Mortars

MECHANISM OF MINERAL ADMIXTURE SUPPRESSING ALKALI-SILICA REACTION .1. CORROSION DEGREE OF REACTIVE AGGREGATE IN BLENDED CEMENT PASTES AND ITS CORRELATIONS WITH EXPANSION VALUE AND ELECTRIC-RESISTANCE CHANGE

Improved Corrosion Resistance of Reinforcing Steel in Mortars Containing Red Mud after Long-Term Exposure to Aggressive Environments