Emission characteristics of nanosized-scandia doped dispenser cathodes at different operating modes

Yiman Wang,Wei Liu,Jinshu Wang,Xizhu Zhang

DOI: https://doi.org/10.1109/IVEC.2011.5747032

2011-01-01

Abstract:Emission properties of nanosized scandia doped dispenser (SDD) cathodes tested at pulse mode with different pulse widths and duty cycles as well as at DC mode are reported and discussed in this paper.

What problem does this paper attempt to address?

Characterization of Scandate Cathode Emission

Xizhu Zhang,Yiman Wang,Jinshu Wang,Wei Liu

DOI: https://doi.org/10.1109/ivelec.2009.5193584

2009-01-01

Abstract:Characterization of emission properties of scandia doped dispenser (SDD) cathodes with Longo-Vaughan equation has been discussed in this paper.
DC Emission Characteristic of Nanosized-Scandia-Doped Impregnated Dispenser Cathodes

Wenlong Liang,Yiman Wang,Jinshu Wang,Wei Liu,Fan Yang

DOI: https://doi.org/10.1109/ted.2014.2319298

IF: 3.1

2014-01-01

IEEE Transactions on Electron Devices

Abstract:To meet the requirements for advanced vacuum electron devices and modern electron beam instruments, dc emission properties of nanosized-scandia-doped impregnated (SDI) cathodes have been investigated in a closely spaced diode configuration system with water-cooled copper anode. The SDI cathodes were made from nanosized-scandia-doped tungsten powder, which was produced by a spray-drying process. A space-charge-limited dc current density of over 60 A/cm(2) has been measured at 950 degrees C-b. An on-going life test with a dc load of 30 A/cm(2) at 950 degrees C-b has completed more than 2000 h of operation to date. The electron cooling for dc beam emission is discussed.
Recent progresses on nanosized-scandia-doped dispenser cathodes

yiman wang,jinshu wang,wei liu,wenlong liang,fan yang

DOI: https://doi.org/10.1109/IVEC.2014.6857485

2014-01-01

Abstract:In this paper, the recent progresses on nanosized-scandia-doped impregnated (SDI) dispenser cathodes made in this research group are reviewed. Spray-drying process, a new method for nonosized-scandia-doped tungsten powder preparation, has been developed. Compared with the formerly used sol-gel technique, the new method results in more controls over the tungsten grain size and morphology. Similar emission level can be reached for the cathodes made from this kind of powder to that of made by sol-gel process. Continuously pulsed emission life test at about 50 A/cm2 has been carried out in a Pierce-gun open structure tube at e beam inc., USA and has been steady for nearly the entire period of 1000 hours. A knee temperature as low as 900 °CB-Mo for initial current density of 58 A/cm2 was estimated from the Miram curve. DC emission has been evaluated in a closely-spaced diode system with water-cooled copper anode. Over 60 A/cm2 space charge limited (SCL) DC current density was repeatedly measured at 950 °CB-Mo. Below this level the DC and pulsed emission are agree well. In DC life test at 950 °CB-Mo, an initial current density of 20 A/cm2 rose gradually to about 30 A/cm2 during first several hundred hours then remained stably for more than 2000 hours. The increase in emission capability has also be verified by a comparison of I/V characters at beginning and 1000 hours of the life test. The improvement of emission performance for SDI cathodes has been correlated to the surface composition changes during life which was performed by in situ surface analysis.
Investigation of Nanosized-Scandia-Doped Dispenser Cathodes with Machined Surfaces

Fan Yang,Jinshu Wang,Yiman Wang,Wei Liu,Xiaoce Zhu

DOI: https://doi.org/10.1109/ted.2016.2528580

IF: 3.1

2016-01-01

IEEE Transactions on Electron Devices

Abstract:Since the cathodes with machined surfaces are required for the practical applications in some high-power vacuum electron devices, the characteristics of nanosized-scandia-doped dispenser (SDD) cathodes with machined surfaces have been investigated, especially in dc applications. In order to reopen the surface pores, which may be smeared by machining procedure, the cathode surface was washed by Ethylene Diamine Tetraacetic Acid (EDTA) solution and prolonged time was taken for the cathode activation. The emission test results show that the SDD cathodes with machined surfaces exhibit better emission performances after treatment. The space-charge-limited dc emission current density of over 20 A/cm(2) at 900 degrees C-b has been measured with temperature compensation for electron cooling after full activation. An on-going life test with a dc load of up to 40 A/cm(2) at 970 degrees C-b has been completed similar to 5000 h of operation to date. Since the emission capability can be fully restored after exposing to air and reactivating for a short time, a preheating procedure is favorable for SDD cathode with machined surface in the practical applications. Surface analysis indicates that a recrystallization of tungsten grains occurs during the prolonged heating process, leading to further reopening of the surface pores. As a result, cathode surface is covered uniformly by active elements of Ba and Sc (as well as O) as on an unmachined surface, thereby maintaining the high emission property of the SDD cathode.
Emission Characteristics of Nanosized Scandia-Doped Dispenser Cathodes in Open Electron-Gun Structures

Wei Liu,Yiman Wang,Jinshu Wang,Yanchun Wang,Bernard Vancil

DOI: https://doi.org/10.1109/ted.2011.2105877

IF: 3.1

2011-01-01

IEEE Transactions on Electron Devices

Abstract:The emission properties of nanosized scandia-doped dispenser cathodes tested in open-structure Pierce electron guns are reported in this paper. Over 100 A/cm(2) and over 80 A/cm(2) space-charge-limited current densities have been obtained at the operating temperatures of 950 degrees C(b) and 1025 degrees C(b) for cathodes with planar emitting surfaces and cathodes with concave emitting surfaces, respectively, at rated anode voltages.
Emission Mechanism of High Current Density Scandia-Doped Dispenser Cathodes

Yiman Wang,Jinshu Wang,Wei Liu,Xizhu Zhang,Lili Li

DOI: https://doi.org/10.1116/1.3609251

2011-01-01

Abstract:The emission mechanism of scandia-doped dispenser (SDD) cathodes is characterized based on systematic investigation of microstructure, surface behavior, evaporation, and emission. High current density SDD cathodes have been developed in recent years to meet the requirements of advanced vacuum electron devices. Space charge limited current densities of over 100 A/cm2 have been reliably reached at a temperature of 950 °Cb. SDD cathodes are composed of a tungsten matrix with submicron structure and uniformly dispersed materials containing Sc, Ba, Ca, Al, and O as nanosized particulates in the matrix. The authors conclude that the copious electron emission from this cathode type results from a layer of Ba–Sc–O on W formed after activation on top of the matrix. This layer is about 100 nm thick and maintains a stable composition over its lifespan. Its emission can be explained in terms of a semiconductor layer with characteristics that differ from a metal-like emission model. The Ba–Sc–O layer is formed by codiffusion of Sc, Ba, and O (generated inside the W-matrix) to the surface of the W-matrix during activation. Furthermore, this layer guarantees a low evaporation rate of emission-relevant materials and thus enables a longer lifespan.
Study of surface nano-particles of scandate cathodes

Xizhu Zhang,Yiman Wang,Jinshu Wang,Wei Liu

DOI: https://doi.org/10.1109/IVESC.2010.5644462

2010-01-01

Abstract:Scandate cathode exhibits the highest emission property among all the thermionic cathodes. Scanadia Doped Dispenser cathode (SDD cathode) is one of the promising cathodes due to its good emission property and reproducibility. The impacts of local electric field enhancement on emission capability of cathode have be considered by applying the actions of Schottky effect and electric field on semiconductor model presented by D. Wright[1]. The calculation results show that the current densities near the spherical nanoparticles are less than 2 times higher than that of the surrounding area. After operating with high current densities at high temperatures for a relative long time, this function was reduced due to the loss of the nanoparticles.
Operation Process of High Current Density Scandia Doped Dispenser Cathodes

Yiman Wang,Wei Liu,Jinshu Wang

DOI: https://doi.org/10.1109/ivesc.2010.5644386

2010-01-01

Abstract:In this paper, operation process of scandia-doped dispenser cathodes is studied based on surface behavior, evaporation and emission properties during preparation, activation, operation and life duration.
Investigation on robustness of Nanosized-Scandia Doped Dispenser Cathodes

Wei Liu,Yiman Wang,Xiaoce Zhu,Yunfei Ynag,Fan Yang,Jinshu Wang

DOI: https://doi.org/10.1109/IVEC.2016.7561805

2016-01-01

Abstract:In order for practical applications in Vacuum Electron Devices (VEDs), the robustness of Scandia Doped Dispenser (SDD) cathodes has been widely concerned. Machinability, emission performance from machined surface, recovery of emission after poisoning; air exposure and ion bombardment have, thereby, been studied. The investigation demonstrated that the cathodes can be successfully machined by normal lathing to the required diameters and curvature radius. A life test with DC loads of up to 40 A/cm 2 at 970 °C b has been completed more than 5000 hours to date for a cathode with machined surface. A full restoring of emission has been proved after the cathodes were exposed to air and reactivated for a short time. This performance allows the cathodes to be pre-heated before assembling into the electron guns. Poisoning experiment evinces that in comparison with that of a 311-XM cathode, which was reported to be less affected by gas poisoning than other M cathode, the poisoning thresholds of residual gases for the SDD cathodes are more than one order of magnitude higher at equivalent temperatures but with higher emission level. The emission and surface behaviour, when an activated cathode encounters ion bombardment at its operating condition, has also been investigated and discussed.
INVESTIGATION OF INFLUENCE OF SURFACE NANOPARTICLE ON EMISSION PROPERTIES OF SCANDIA-DOPED DISPENSER CATHODES

Xizhu Zhang,Jinshu Wang,Yiman Wang,Wei Liu,Meiling Zhou,Zhiyuan Gao

DOI: https://doi.org/10.1142/s1793604713500409

IF: 1.4901

2013-01-01

Functional Materials Letters

Abstract:The microstructure of a fully activated scandia doped dispenser (SDD) cathode has been studied by scanning electron microscope (SEM). The observation results display that nanoparticles appear at the growth steps and the surface of tungsten grains of the fully activated SDD cathode. To study the influence of the nanoparticles on the emission, the local electric field strengths around the nanoparticles have been calculated by Maxwell 2D code and Comsol. The calculation results show that the local electric field strengths are enhanced by 1.1 to 3.8 times to average value based on different model conditions. The highest field strength is about 1.54 × 105 V/cm at an average field strength of 40 KV/cm, which is related to a space-charge limited (SCL) current density of 100 A/cm2 in the experimental configuration. This implies the field strength is not high enough to cause field emission.
Character And Application Of Scandia Doped Dispenser Cathodes With Concave Surfaces

wei liu,fan yang,yiman wang,xiaoce zhu,xiang liu,jinshu wang

DOI: https://doi.org/10.1109/ivec.2015.7223902

2015-01-01

Abstract:Since the cathodes with concave surfaces are required for the practical applications in most high-power vacuum electron devices, characteristics of nanosized-Scandia Doped Dispenser (SDD) cathodes with concave surfaces have been investigated, especially in dc applications. A space charge-limited (SCL) dc current density of over 50 A/cm(2) has been measured at 1000 degrees C-b. An on-going life test with a dc load of up to 40 A/cm(2) at 970 degrees C-b has been completed about 3000 hours of operation to date. The emission performance of the cathode was further evaluated in an electron gun test tube, which is a part of an mm wave CW-TWT, before the practical application in the real devices.
P3-37: Emission characteristics of Sc- doped dispenser cathodes in electron gun open structures

Wei Liu,Yiman Wang,Lei Zhao,Lili Li,Xizhu Zhang,Jinshu Wang

DOI: https://doi.org/10.1109/IVELEC.2010.5503378

2010-01-01

Abstract:Emission properties of Scandia Doped Dispenser (SDD) cathodes tested in Pierce Gun open structures have been reported in this paper. 80-100 A/cm2 Space-Charge Limited (SCL) current densities have been obtained at designed anode voltages and normal operating temperatures for cathodes with either flat surfaces or concave surfaces. The influences of anode effects on cathodes, which appear in close-spaced diodes, are discussed in the paper.
Electron Emission of Scandia-Doped Dispenser Cathodes

WANG Hui,LI Ji,PAN Ke-xin,LIAN Yan-qiang,WANG Jin-shu,WANG Yi-man,LIU Wei

DOI: https://doi.org/10.3969/j.issn.1002-8935.2006.05.005

2006-01-01

Abstract:The scandia-doped dispenser cathodes were tested in the planar diode with a water cooling anode.The results indicate that its current density is far higher than that of the other kinds of cathodes.The cathode presented in this paper has a work function of 1.55 eV with a electron emission constant of 1.126 A/cm~2K~2 at 849℃.Miram plot is used to investigate the under-heating characteristics and the electron emission property of the cathode.
Robustness Investigation on Nanosized-Scandia-Doped Dispenser Cathodes

Yunfei Yang,Yiman Wang,Wei Liu,Zhaoliu Pan,Junhui Li,Jinshu Wang

DOI: https://doi.org/10.1109/ted.2018.2814542

2018-01-01

Abstract:In order for practical applications in vacuum electron devices, the robustness of scandia-doped dispenser (SDD) cathode is a major concern. Emission properties after air exposure and gas poisoning have, therefore, been studied. A full restoring of emission has been proved after the cathodes were exposed to air and reactivated for a time much shorter than initial activation. Poisoning experiments demonstrated that the poisoning pressure thresholds of residual gases for the SDD cathode are about half to one order of magnitude higher at equivalent temperatures but with higher emission level in comparison with that of an excellent M cathode. The cathode is easier to recover after poisoning and can operate stably in a nonideal environment. These features are thought to be related to the surface Ba-Sc-O structure which has closely chemical association, better stability for air exposure, relatively high tolerance to gas poisoning, and the semiconductor emission characteristic.
Investigation of Sc2O3 Contents for Nano-sized Scandia Doped Dispenser Cathode

Zhaoliu Pan,Yiman Wang,Yunfei Yang,Jinshu Wang

DOI: https://doi.org/10.1109/ivec.2018.8391630

2018-01-01

Abstract:Nano-sized Scandia Doped Dispenser cathode made from Scandia doped tungsten powder has been paid worldwide attention due to its high emission and satisfactory emission uniformity. Among the adopted doping techniques the liquid-liquid doping by Sol-Gel process is the most favorable for the performance of this kind of cathode. A further searching on the details of the processes is necessary for cathode manufacturing. In this study, Sc2O3 contents of 1% wt., 3% wt., 5% wt. and 7% wt. (named Sc1, Sc3, Sc5 and Sc7) were added to the tungsten powder; their effects on microstructures and emission performance of the produced cathodes were investigated. The study proved that the nano-sized Sc2O3 particles are getting richer from Sc1 to Sc7 but cover on the W grains in all cases. While there is a slight decrease in porosities from Sc1 to Sc7, the filled impregnant of Ba Ca aluminates for Sc1 to Sc5 is satisfied the requirement for dispenser cathode, but is obviously lower for Sc7. All cathodes made from Sc3, Sc5 and Sc7 reach a Space Charge Limited current density of about 50A/cm(2) at true temperature of 960 degrees C except Sc1 of 33A/cm(2). The knee points at initial current density of 30A/cm(2) are 830 degrees C, 875 degrees C and 920 degrees C for Sc5, Sc3 and Sc7, respectively. Almost no knee can be observed for Sc1. Therefore, Sc5 and Sc3 exhibit the best emission and emission uniformity, Sc7 comes second and Sc1 goes the worst.
Correlation of emission behavior and surface feature of Scandia doped dispenser cathodes

jinshu wang,yanchun wang,lili li,wei liu,xizhu zhang

DOI: https://doi.org/10.1109/IVELEC.2008.4556419

2008-01-01

Abstract:In this work we investigated the correlation between the emission properties of Scandia doped dispenser cathodes and their surface features. A proposal for explanation of the observed phenomena has been suggested.
A review on scandia doped tungsten matrix scandate cathode

Jinshu Wang,Yunfei Yang,Yiman Wang,Wei Liu,Meiling Zhou,Tieyong Zuo

DOI: https://doi.org/10.1007/s42864-019-00007-8

2019-01-01

Tungsten

Abstract:As the cathode with the highest electron emission capability in the thermionic cathode, the scandate cathode has attracted more and more attention in recent years, especially the scandia doped tungsten matrix scandate cathode. Experimental studies show that scandia doped tungsten matrix scandate cathodes with submicron microstructures exhibit excellent emission capacity, and the pulse emission current density in the space-charge region can be over 35 A cm −2 at 850 °C b . In the direct current (DC) condition with temperature compensation, the emission current density could reach 25 A cm −2 at 850 °C b . The device lifetime is over 3700 h after operating at 950 °C b with the DC loading of 40 A cm −2 . The emission mechanism of the scandate cathode including the effect of the surface structure and composition on the work function of the cathode are systematically reviewed.
Investigation of Sc<inf>2</inf> O<inf>3</inf> contents for nano-sized Scandia doped dispenser cathode

Zhaoliu Pan,Yiman Wang,Yunfei Yang,Jinshu Wang

DOI: https://doi.org/10.1109/IVEC.2018.8391630

2018-01-01

Abstract:Nano-sized Scandia Doped Dispenser cathode made from Scandia doped tungsten powder has been paid worldwide attention due to its high emission and satisfactory emission uniformity. Among the adopted doping techniques the liquid-liquid doping by Sol-Gel process is the most favorable for the performance of this kind of cathode. A further searching on the details of the processes is necessary for cathode manufacturing. In this study, Sc 2 O 3 contents of 1%wt., 3%wt., 5%wt. and 7%wt. (named Sc1, Sc3, Sc5 and Sc7) were added to the tungsten powder; their effects on microstructures and emission performance of the produced cathodes were investigated. The study proved that the nano-sized Sc 2 O 3 particles are getting richer from Sc1 to Sc7 but cover on the W grains in all cases. While there is a slight decrease in porosities from Sc1 to Sc7, the filled impregnant of Ba Ca aluminates for Sc1 to Sc5 is satisfied the requirement for dispenser cathode, but is obviously lower for Sc7. All cathodes made from Sc3, Sc5 and Sc7 reach a Space Charge Limited current density of about 50A/cm 2 at true temperature of 960°C except Sc1 of 33A/cm 2 . The knee points at initial current density of 30A/cm 2 are 830C, 875°C and 920°C for Sc5, Sc3 and Sc7, respectively. Almost no knee can be observed for Sc1. Therefore, Sc5 and Sc3 exhibit the best emission and emission uniformity, Sc7 comes second and Sc1 goes the worst.
Surface characteristics of scandate dispenser cathodes during life

Jinshu Wang,Yiman Wang,Xi Wang,Xizhu Zhang

DOI: https://doi.org/10.1109/IVEC.2013.6571168

2013-01-01

Abstract:To find the changes of surface compositions during life time of the Scandia-doped impregnated dispenser cathodes, two cathodes have been tested at an activation temperature of 1150°CB-Mo and an operation temperature of 1000°CB-Mo , respectively, in an AES system up to more than 7,000 hours. Surface compositions were monitored in-situ at intervals. The tested results have been reported and discussed in this paper.
Effect of Scandia Doping Method on the Emission Uniformity of Scandate Cathode with Sc2O3–W Matrix

Jinshu Wang,Chen Lai,Wei Liu,Fan Yang,Xizhu Zhang,Yuntao Cui,Meiling Zhou

DOI: https://doi.org/10.1016/j.materresbull.2013.05.069

IF: 5.6

2013-01-01

Materials Research Bulletin

Abstract:Scandia doped tungsten matrix dispenser cathodes were manufactured using scandia doped tungsten powder prepared by mechanical mixing, liquid-solid doping and a spray drying method. It is found the macrostructure of the cathode depended on the powder preparation method. The cathode prepared using the powder prepared by spray drying method had a homogenous and porous matrix characterized with grains with a diameter of less than 1 pm and with many nanoparticles distributing uniformly around these grains. The cathode with submicron structure and uniform distribution of scandia exhibited good emission uniformity. The emission uniformity Delta J/J of the cathode prepared by spray drying method was 0.17, about 6 times lower than that of the cathode prepared by mechanical mixing method. The calculation results showed that the nanoparticles led to electric field enhancement. A Ba-Sc-O multilayer on the cathode surface and nanoparticles distributing mainly on W grains contributed to the emission property of the cathode. (C) 2013 Elsevier Ltd. All rights reserved.

Emission characteristics of nanosized-scandia doped dispenser cathodes at different operating modes

Characterization of Scandate Cathode Emission

DC Emission Characteristic of Nanosized-Scandia-Doped Impregnated Dispenser Cathodes

Recent progresses on nanosized-scandia-doped dispenser cathodes

Investigation of Nanosized-Scandia-Doped Dispenser Cathodes with Machined Surfaces

Emission Characteristics of Nanosized Scandia-Doped Dispenser Cathodes in Open Electron-Gun Structures

Emission Mechanism of High Current Density Scandia-Doped Dispenser Cathodes

Study of surface nano-particles of scandate cathodes

Operation Process of High Current Density Scandia Doped Dispenser Cathodes

Investigation on robustness of Nanosized-Scandia Doped Dispenser Cathodes

INVESTIGATION OF INFLUENCE OF SURFACE NANOPARTICLE ON EMISSION PROPERTIES OF SCANDIA-DOPED DISPENSER CATHODES

Character And Application Of Scandia Doped Dispenser Cathodes With Concave Surfaces

P3-37: Emission characteristics of Sc- doped dispenser cathodes in electron gun open structures

Electron Emission of Scandia-Doped Dispenser Cathodes

Robustness Investigation on Nanosized-Scandia-Doped Dispenser Cathodes

Investigation of Sc2O3 Contents for Nano-sized Scandia Doped Dispenser Cathode

Correlation of emission behavior and surface feature of Scandia doped dispenser cathodes

A review on scandia doped tungsten matrix scandate cathode

Investigation of Sc<inf>2</inf> O<inf>3</inf> contents for nano-sized Scandia doped dispenser cathode

Surface characteristics of scandate dispenser cathodes during life

Effect of Scandia Doping Method on the Emission Uniformity of Scandate Cathode with Sc2O3–W Matrix