Abstract:Abstract Central cracking in cross-wedge-rolled workpieces results in high wastage and economic loss. Recent cross-wedge rolling tests on two batches of steel showed that one batch formed central cracks, while the other was crack-free. The batches were both nominally of the same chemical composition and thermomechanical treatment history. In addition, both batches had passed all the standard quality assessments set for conventional forging processes. It was suspected that the different cracking behaviours were due to differences in microstructure between the two as-received steel billets, and the material in cross-wedge rolling (CWR) was more sensitive to the initial microstructure compared with other forging processes due to its specific loading condition including ostensibly compression and large plastic strain. Nevertheless, no previous study of this important problem could be identified. The aim of this study is, therefore, to identify the key microstructural features determining the central crack formation behaviour in CWR. The hot workability of the as-received billets was studied under uniaxial tensile conditions using a Gleeble 3800 test machine. Scanning electron microscope with energy-dispersive X-ray spectroscopy and electron backscatter diffraction was applied to characterise, quantitatively analyse, and compare the chemical composition, phase, grain, and inclusions in these two billets, both at room temperature and also at the CWR temperature (1080 °C). Non-metallic inclusions (oxides, sulphides, and silicates) in the billets were determined to be the main cause of the reported central cracking problem. The ductility of the steels at both room and elevated temperatures deteriorated markedly in the presence of the large volumes of inclusions. Grain boundary embrittlement occurred at the CWR temperature due to the aggregation of inclusions along the grain boundaries. It is suggested that a standard on specifying the inclusion quantity and size in CWR billets be established to produce crack-free products.

Numerical and experimental research on warm cross wedge rolling of hollow shafts with corrugated surface

Investigation on the inner hole spiral-groove of cross wedge rolling of hollow shafts with mandrel

Design and simulation of cross wedge rolling process for hollow motor shaft

Microstructure and mechanical properties of TC4 titanium alloy hollow shaft formed by cross wedge rolling

Feasibility Analysis of Cross Wedge Rolling (CWR) of Hexahedral Billet

Formability and microstructure of TC4 titanium alloy hollow shafts formed by cross-wedge rolling with a mandrel

Microstructural effects on central crack formation in hot cross-wedge-rolled high-strength steel parts

Numerical and experimental analysis of defects control in cross wedge rolling for titanium alloy workpieces

Numerical Analysis and Parameter Optimization of Wear Characteristics of Titanium Alloy Cross Wedge Rolling Die

The Mechanism of Forming Hollow Shafts with Constant Wall Thickness by Three-Roll Skew Rolling

Investigation on the formation of central damage in cross wedge rolling of GH4169 alloy

Study on necking defects, microstructure and mechanical properties of TC4 alloy by cross wedge rolling

A Multi-scale Modelling by Coupling Cellular Automata with Finite Element Method and Its Application on Cross-Wedge Rolling

Novel evaluation method for metal workability during cross wedge rolling process

Three-dimensional rigid–plastic finite element simulation for the two-roll cross-wedge rolling process

ON FORGING FORMING FORCE IN THE COMPOSITE TECHNOLOGY OF CROSS WEDGE ROLLING ( CWR ) AND FORGING FOR UNIVERSAL JOINT FORK

Investigation and prediction of central cracking in cross wedge rolling

Effect of warm forming process parameters on 42CrMo4 skew rolled bar mechanical properties and microstructure

Internal defects control mechanism and process optimization of TC11 titanium alloy by cross wedge rolling

Experimental and numerical investigations on the deformation defects by gear rolling process with local induction heating

Effect of Hot-Rolling Deformation on Microstructure and Sliding Wear of High-Chromium Cast Iron