Abstract:Nano-ZSM-5 with large amount and high strength of acid sites were successfully synthesized by hydrothermal crystallization of pure-silica nucleus in NaAlO2 alkali solution. The concentration of NaAlO2 alkali solution was decreased by increasing the H2O/Al ratio from 200 to 2600, which strongly determined the acidic properties and crystal size of the obtained nano-ZSM-5. Low concentration of NaAlO2 alkali solution was found unfavorable for the incorporation of Al into the bulk of ZSM-5 crystal in crystallization process. Hence, more Al distributed at the exterior of crystals, which enhanced the accessibility of the acid sites during reaction. Large amount and high strength of acid sites were produced for nano-ZSM-5 by increasing H2O/Al ratio. When the H2O/Al ratio increased from 200 to 2600, the total amount of acid sites increased from 0.59 to 0.81 mmol g(-1), much higher than conventional value of 0.50 mmol g(-1). In addition, the acid strength increased and the ratio of Bronsted/Lewis acid sites were sharply increased from 2.3 to 4.1 when the H2O/Al ratio increased. Moreover, the size of nano-crystal was also decreased by above decreasing the concentration of the NaAlO2 alkali solution. When the H2O/Al ratio was 2600, the obtained sample possessed total acid amount of 0.81 mmol g(-1) and crystal size of 60 nm, respectively. Methanol to hydrocarbon (MTH) reaction results showed that the increased acid sites of the catalyst decreased its catalytic lifetime to some extent, but the aromatics selectivity was tunable obviously. As for the catalyst prepared with H2O/Al ratio of 2000, the aromatics selectivity of the obtained catalyst reached to 66.0%. This paper provided a method for the fabrication of small-size nano-ZSM-5 with large amount and high strength of acid sites and regulated Al distribution for MTH reaction.

ZSM-5 nanocrystal promoted low-temperature activity of supported manganese oxides for catalytic oxidation of toluene

Adsorption and Catalytic Ozonation of Toluene on Mn/ZSM-5 at Low Temperature

In Situ Fabrication of Highly Active Γ-Mno2/smmno3 Catalyst for Deep Catalytic Oxidation of Gaseous Benzene, Ethylbenzene, Toluene, and O-Xylene.

Enhanced catalytic oxidation of toluene over manganese-based multi-metal oxides synthesized by ozone driving redox reaction

Bimetallic Fe-Mn loaded H-ZSM-5 zeolites for excellent VOCs catalytic oxidation at low-temperatures: Synergistic effects and catalytic mechanisms

Rational Design of Bimetal Mn-Ce Nanosheets Anchored on Porous Nano-sized ZSM-5 Zeolite for Adsorption-Enhanced Catalytic Oxidation of Toluene

Catalytic Performance for Toluene Abatement over Al-rich Beta Zeolite Supported Manganese Oxides

Facile synthesis of ultrafine nanosized ZSM-5 zeolite using a hydroxyl radical initiator for enhanced catalytic performance in the MTG reaction

MCM-41 supported Cu-Mn catalysts for catalytic oxidation of toluene at low temperatures.

Pt-loaded ellipsoidal nanozeolite as an active catalyst for toluene catalytic combustion

Synthesis of Nanoscale ZSM-5 Zeolites for the Catalytic Cracking of Oleic Acid into Light Olefins and Aromatics

Size controllable synthesis of ZSM-5 zeolite and its catalytic performance in the reaction of methanol conversion to aromatics

Tuning the crystallinity of the MnOx catalysts to promote toluene catalytic oxidation

Controllable Synthesis of Nano-Zsm-5 Catalysts with Large Amount and High Strength of Acid Sites for Conversion of Methanol to Hydrocarbons

Tuning smaller Co3O4 nanoparticles onto HZSM-5 zeolite via complexing agents for boosting toluene oxidation performance

ZrO 2 -Supported Α-Mno 2 :Improving Low-Temperature Activity and Stability for Catalytic Oxidation of Methane

Low-content Pt loading on a post-treatment-free zeolite for efficient catalytic combustion of toluene

The reaction mechanism of highly dispersed Cu atoms and ultrafine MnOx nanoclusters co-modified ZSM-5 based on in-situ heteronuclear substitution for catalytic oxidation C6H14

Catalytic oxidation of toluene over ZIF-8 composited with Mn by different methods

Effects of the metal ionic radius at lattice site on surface active oxygen and reducibility over doped mesoporous ZSM-5 for catalytic oxidation VOC

Synergistic Effect of Pt Nanoparticles and Micro-Mesoporous ZSM-5 in VOCs Low-Temperature Removal