Microwave-Assisted Preparation of the Cubic RuSe 2 /C Catalyst for Fuel Cell Applications

Qing Gong,Peng Hu,Weifeng Yang,Tengfei Zhang,Jiaqi Liu,Hengyi Li,Xuan Cheng

DOI: https://doi.org/10.1021/acsaem.1c03990

IF: 6.4

2022-11-01

ACS Applied Energy Materials

Abstract:Achieving the desired performance in terms of activity and durability toward oxygen reduction reaction (ORR) is a grand challenge for ruthenium (Ru) selenides. In this work, by regulating the molar ratio of selenium (Se) to Ru (1.5 ≤ Se/Ru ≤ 3.5), a facile method involving a simple microwave route followed by heat treatment was developed to synthesize cubic RuSe2/C electrocatalysts. A mixed phase of predominant cubic RuSe2 with minor hexagonal Ru was identified for RuSe2/C (Se/Ru ≤ 2.0) catalysts, while a mixed phase of predominant cubic RuSe2 with minor hexagonal Se for RuSe2/C (Se/Ru ≥ 2.5) catalysts. A slightly Se-rich (Se/Ru ≤ 2.5) surface would prevent RuSe2 nanoparticles from growing, while too much Se (Se/Ru ≥ 3.0) would cause the aggregation of RuSe2 nanoparticles. The RuSe2/C catalyst prepared using Se/Ru = 2.5 demonstrated the best ORR activity, showing the half-wave potentials of 0.71 and 0.77 V in HClO4 and KOH solutions, respectively, with excellent methanol tolerance. Furthermore, this best-performed catalyst delivered a maximum power density of 353 mW·cm–2 at 1600 mA·cm–2 when tested as a cathode catalyst in a H2/O2 single cell with an impressive Ru utilization of 1961 mW·mg–1. Fuel cell performance decayed by 33.7% after holding the current density at 400 mA·cm–2 for 55 h, which might be attributed to the severe aggregation of RuSe2 nanoparticles and harmful Se migration from the cathode side to the anode side, resulting from the dissolution of Se from the catalyst surface.

materials science, multidisciplinary,chemistry, physical,energy & fuels