Abstract:Highly porous and hydrophobic silica aerogel is fabricated using fly ash and trona ore as the starting materials and the cost-effective ambient pressure drying technique. The optimal calcination parameters are determined as temperature of 850°C, holding time of 2h, and the trona ore/fly ash mass ratio of 1.4. The CO2 release mechanism during calcination is proposed and has been verified by the Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) and X-ray fluorescence (XRF) technique. The hydrogel is derived from reacting the calcination mixture with sulphuric acid solution, followed by filtration. The impurities can be effectively removed through water washing and solvent exchange processes. No ion exchange resin is used in this preparation method, and thus it is a safe, inexpensive and much more straightforward process. In order to minimize drying shrinkage, the hydrogel is first transformed into an alcogel by soaking in ethanol, after which the alcogel is surface modified with the hexane/ethanol/trimethylchlorosilane (hexane/ethanol/TMCS) mixture solution. It has been observed that the specific surface area, BJH desorption pore volume, and BJH desorption average pore diameter all first increase and then decrease so that reach to the maximum values once the heat treatment temperature approaches 500°C due to the oxidation of CH3 groups on the silica skeleton surface. The final product presents special characteristics including: (1) high thermal stability for maintaining hydrophobicity up to 476°C, (2) contact angle of the as-dried silica aerogel as high as 151°, (3) silica particle size of ca. 3–6nm, agreeing well with the model as reported, (4) and the 500°C heat treated sample possessing a large specific surface area of 856.2m2/g, a large pore volume of 2.92cm3/g, and a BJH desorption average pore diameter of 17.1nm. The proposed inexpensive approach produces silica aerogel with superior properties and is a scalable-manufacturing method for large-scale industrial production.

Transformation of Fly Ash-Based Oxide Particles into a Functional Silica-Alumina Aerogel and Its Potential Application as an Anti-icing Surface

Nanoporous Silica–Chitosan Aerogels for Thermal Insulation and Flame Retardancy

Synthesis and Surface Strengthening Modification of Silica Aerogel from Fly Ash

Synthesis and Characterization of Silica Aerogel and Its Composite Materials

Rapid Synthesis of Super Insulation Silica Aerogel Composites Strengthened with Mullite Fibers

Ambient Pressure Drying as an Advanced Approach to the Synthesis of Silica Aerogel Composite for Building Thermal Insulation

Energy effective utilization of circulating fluidized bed fly ash to prepare silicon-aluminum composite aerogel and gypsum

Fumed Silica-Derived, Ambient Dried, and Low-Cost Nanoporous Aerogel-like Monoliths for Thermal Insulation

Recycling Coal Fly Ash for Super-Thermal-Insulating Aerogel Fiber Preparation with Simultaneous Al2O3 Extraction

Recycling Coal Fly Ash for Super-Thermal-Insulating Aerogel Fiber Preparation with Simultaneous Al 2 O 3 Extraction.

In-situ acid catalysis strategy to achieve rapid ambient pressure drying preparation of aerogels

A Facile Strategy for Freeze-Drying Preparation of Silica Aerogel from Sodium Silicate

Anisotropic and high-strength SiO2/cellulose nanofiber composite aerogel with thermal superinsulation and superhydrophobicity

Radiation Synthesis of Carbon/Aluminum/Silica Aerogel Nanoporous Structure Derived from Polyacrylamide Hydrogel for High Temperature and Oil Removal Applications

Fabrication and characterization of Aerogel-Polydimethyl siloxane (PDMS) Insulation Film

Ultrasound‐assisted freeze‐drying strategy to enhance nanoparticle dispersion in aerogels: A case study on polyimide/silica nanocomposite aerogel

A novel low-cost method of silica aerogel fabrication using fly ash and trona ore with ambient pressure drying technique

High Compression Strength and Thermal Insulation Silica Aerogel Monolith with Scaffold of a Cyclic Olefin Siloxane Co-Oligomer Via Ambient Pressure Drying

Spray Freeze-Dried Monolithic Silica Aerogel Based on Water-Glass with Thermal Superinsulating Properties

One-Pot Sol–Gel Synthesis of Highly Insulative Hybrid P(AAm-CO-AAc)-Silica Aerogels with Improved Mechanical and Thermal Properties

Spraying Fabrication of Durable and Transparent Coatings for Anti-Icing Application: Dynamic Water Repellency, Icing Delay, and Ice Adhesion