Abstract:Aerogel has been widely known as a low-density and highly porous material and is closely connected with the complex processing methods, such as freeze–drying or supercritical drying. In this work, using the polymerization-induced aramid nanofiber (PANF) as a building block, we put forward a modified freezing–drying method for the high-efficiency preparation of all-<i>para</i>-aromatic-amide aerogels. In the preparation process, PANF hydrogel is first frozen at −18 °C and then dried at 20–150 °C for the formation of PANF aerogel. The PANF framework formed during the freezing process is crucial for the formation of the PANF aerogel. Moreover, the space-occupying effect of ice crystals is also helpful for the formation of the macroscopic pore structure in the aerogel. Aerogels with large size or well-controlled shape could be successfully obtained by this method. Through the variation of PANF concentration in the hydrogel and drying temperature, aerogels with different densities (20–185 mg/cm<sup>3</sup>) could be achieved, and the lowest density is reached at 150 °C, with the PANF concentration of 0.7%. The low-density PANF aerogels show high specific compressive strengths and low thermal conductivities, which are comparable to those resulting from the freeze–drying or supercritical drying method. Furthermore, the shrinkage phenomenon in the drying process could be skillfully utilized for the preparation of PANF aerogel-coated objects. The PANF aerogels could be applied as a thermal insulating material or shock absorption material in practical applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c01551?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c01551</a>.Figure S1–S16: statistics of the diameter of PANFs; repeated filtering-dispersing process and PANF hydrogels with different PANF concentration; different products obtained from different methods; macroscopic state of PANF hydrogel and thawed PANF hydrogel before and after magnetic stirring; PANF hydrogel and the corresponding PANF aerogel in the shape of mooncake; preparation process of PANF aerogel-coated quartz tube; SEM images of different PANF aerogels at a low (×50) and high (×50000) magnification; high-temperature (150 °C) drying experiment for unfrozen and frozen PANF hydrogels with PANF% = 0.7%; specific strength of different PANF aerogel samples (ε = 70%); specific strength comparison of PA-20 and PA-40 with the low-density ANF-based aerogels (ε = 30%); compressive stress–strain curves of PA-20 at different strains for 100 compression–decompression cycles; surface of PANF aerogel before and after heating by infrared ray bulb; temperature variations of water in the metal tubes (with or without PANF aerogel insulation layer) after heating by infrared ray bulb; profiles of PANF aerogel and PU foam in the hot stage heating test; TGA and DTA curves of PANF aerogel and PU foam in air atmosphere; Tables S1–S3: stress retention and height recovery rates of PA-20 after 100 compression–decompression cycles at different strains; thermal conductivities of PANF aerogels and the already reported aramid aerogels; specific strengths (ε = 70%) and thermal conductivities of different kinds of aerogels (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c01551/suppl_file/nn1c01551_si_001.pdf">PDF</a>)Movie S1: Drop test of the PANF aerogel-coated quartz tube (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c01551/suppl_file/nn1c01551_si_002.avi">AVI</a>)This article has not yet been cited by other publications.

Ultrasound‐assisted freeze‐drying strategy to enhance nanoparticle dispersion in aerogels: A case study on polyimide/silica nanocomposite aerogel

Ultrasound-assisted freeze-drying process for polyimide aerogels

A Facile Strategy for Freeze-Drying Preparation of Silica Aerogel from Sodium Silicate

Konjac glucomannan-based aerogels with excellent thermal stability and flame retardancy for thermal insulation application

Transparent, Ultraflexible, and Superinsulating Nanofibrous Biocomposite Aerogels Via Ambient Pressure Drying

Flexible and Compressible Nanostructure-Assembled Aramid Nanofiber/Silica Composites Aerogel

Physical Fields Coupling Freeze‐Drying Process of Carbon‐Based Composite Aerogels for Microwave Absorption and Electromagnetic Interference Shielding

Double-cross-linking Strategy for Preparing Flexible, Robust, and Multifunctional Polyimide Aerogel

Facile strategy to prepare polyimide nanofiber assembled aerogel for effective airborne particles filtration

Fabrication of Elastic Silica-Bacterial Cellulose Composite Aerogels with Nanoscale Interpenetrating Network by Ultrafast Evaporative Drying

High Compression Strength and Thermal Insulation Silica Aerogel Monolith with Scaffold of a Cyclic Olefin Siloxane Co-Oligomer Via Ambient Pressure Drying

In-situ acid catalysis strategy to achieve rapid ambient pressure drying preparation of aerogels

Fumed Silica-Derived, Ambient Dried, and Low-Cost Nanoporous Aerogel-like Monoliths for Thermal Insulation

Cellulose Nanofibril (CNF) Based Aerogels Prepared by a Facile Process and the Investigation of Thermal Insulation Performance

Robust-flexible and highly-thermostable polyimide-silica aerogels with adjustable fiber skeleton structure for efficient aerospace thermal protection

SiO 2 Nanostructure-Based Aerogels with High Strength and Deformability for Thermal Insulation

Ultrahigh-strength silicone aerogels reinforced by an armor-like epoxy framework via a temperature-controlled sequential reaction strategy

Multiscale Nanocelluloses Hybrid Aerogels for Thermal Insulation: the Study on Mechanical and Thermal Properties.

Robust Silica–Agarose Composite Aerogels with Interpenetrating Network Structure by in Situ Sol–Gel Process

Ultralight, thermal insulating, and high-temperature-resistant mullite-based nanofibrous aerogels

Macroscopic-Scale Preparation of Aramid Nanofiber Aerogel by Modified Freezing–Drying Method