Abstract:It is revealed that a CoZr2 superconductor exhibits volumetric negative thermal expansion (NTE) under high pressure. The volumetric NTE arises from the suppressed positive thermal expansion (PTE) along the a‐axis and robust NTE along the c‐axis. The volumetric NTE in superconductors can be utilized in superconducting devices with robust to wide‐range temperature cycle. The superconductivity is observed under high pressure through electrical resistance measurements. The study investigates the thermal expansion and superconducting properties of a CuAl2‐type (tetragonal) superconductor CoZr2 under high pressures. High‐pressure synchrotron X‐ray diffraction is performed in a pressure range of 2.9 GPa < P < 10.4 GPa, and it is discovered that CoZr2 exhibits volumetric negative thermal expansion (NTE) under high pressures. Although uniaxial positive thermal expansion (PTE) along the a‐axis is observed under ambient pressure, it is suppressed by pressure, whereas a large uniaxial NTE along the c‐axis is maintained under the pressure regime. Because of the combination of the suppressed uniaxial PTE along the a‐axis and uniaxial NTE along the c‐axis, volumetric NTE is achieved under high pressure in CoZr2. The volumetric NTE mechanism is based on the flexible crystal structure caused by the soft Co–Co bond, as observed in the isostructural compound FeZr2, which exhibits a uniaxial NTE along the c‐axis. High‐pressure electrical resistance measurements of CoZr2 are performed and confirm superconductivity at 0.03 GPa < P < 41.9 GPa. Because of the coexistence of the two phenomena, volumetric NTE and superconductivity, in CoZr2 under high pressure, coexistence can be achieved under ambient pressure by tuning the chemical composition after the present observation.

Sign change in c-axis thermal expansion and lattice collapse by Ni substitution in Co1-xNixZr2 superconductors

Sign change in c-axis thermal expansion constant and lattice collapse by Ni substitution in transition-metal zirconide superconductor Co1-xNixZr2

Anisotropic Chemical Expansion Of La1-Xsrxcoo3-Delta

Anisotropic Chemical Expansion of La1–xSrxCoO3−δ

Anomalous thermal expansion in a CuAl2-type superconductor CoZr2

Uniaxial negative thermal expansion in an orthorhombic superconductor CoZr3

Pressure-induced volumetric negative thermal expansion in CoZr2 superconductor

Specific heat analyses on optical-phonon-derived uniaxial negative thermal expansion system $Tr$Zr$_{2}$ ($Tr$ = Fe and Co$_{1-x}$Ni$_{x}$)

Pressure‐Induced Volumetric Negative Thermal Expansion in CoZr2 Superconductor

Axis thermal expansion switching in transition-metal zirconides TrZr2 by tuning the c/a ratio

Uniaxial negative thermal expansion in a tetragonal V3S-type superconductor IrZr3

Specific heat analyses on optical-phonon-derived uniaxial negative thermal expansion system TrZr2 (tr = fe and Co1− xNix)

Superconducting properties and electronic structure of CuAl2-type transition-metal zirconide Fe1-xNixZr2

Structural And Magnetic Studies Of Co1-Xnixcr2o4 (0 <= X <= 1)

An ant-based algorithm for annular sorting

Charge transfer and local structure distortion in Zn-doped LaFe 1−x Co x AsO

Te substitution effect in low-dimensional superconductor NbSe 2-xTex (x= 0,0.1,0.2)

Enhanced Negative Thermal Expansion Induced by Simultaneous Charge Transfer and Polar-Nonpolar Transitions

Thermal Expansion Anomaly in High Tc La1.85Sr0.15CuO4 Associated with the Superconductivity

Effects of Co substitution on the structural and magnetic properties of Sr(Ni$_{1-x}$Co$_x$)$_2$P$_2$

Thermal Expansion and Compressibility in Superconducting NaxCoO2o4xD2O (x?1/3): Evidence for Pressure-Induced Charge Redistribution