Abstract:It is revealed that a CoZr2 superconductor exhibits volumetric negative thermal expansion (NTE) under high pressure. The volumetric NTE arises from the suppressed positive thermal expansion (PTE) along the a‐axis and robust NTE along the c‐axis. The volumetric NTE in superconductors can be utilized in superconducting devices with robust to wide‐range temperature cycle. The superconductivity is observed under high pressure through electrical resistance measurements. The study investigates the thermal expansion and superconducting properties of a CuAl2‐type (tetragonal) superconductor CoZr2 under high pressures. High‐pressure synchrotron X‐ray diffraction is performed in a pressure range of 2.9 GPa < P < 10.4 GPa, and it is discovered that CoZr2 exhibits volumetric negative thermal expansion (NTE) under high pressures. Although uniaxial positive thermal expansion (PTE) along the a‐axis is observed under ambient pressure, it is suppressed by pressure, whereas a large uniaxial NTE along the c‐axis is maintained under the pressure regime. Because of the combination of the suppressed uniaxial PTE along the a‐axis and uniaxial NTE along the c‐axis, volumetric NTE is achieved under high pressure in CoZr2. The volumetric NTE mechanism is based on the flexible crystal structure caused by the soft Co–Co bond, as observed in the isostructural compound FeZr2, which exhibits a uniaxial NTE along the c‐axis. High‐pressure electrical resistance measurements of CoZr2 are performed and confirm superconductivity at 0.03 GPa < P < 41.9 GPa. Because of the coexistence of the two phenomena, volumetric NTE and superconductivity, in CoZr2 under high pressure, coexistence can be achieved under ambient pressure by tuning the chemical composition after the present observation.

Anomalous thermal expansion in a CuAl2-type superconductor CoZr2

Uniaxial negative thermal expansion in an orthorhombic superconductor CoZr3

Axis thermal expansion switching in transition-metal zirconides TrZr2 by tuning the c/a ratio

Uniaxial negative thermal expansion in a tetragonal V3S-type superconductor IrZr3

Sign change in c-axis thermal expansion constant and lattice collapse by Ni substitution in transition-metal zirconide superconductor Co1-xNixZr2

Specific heat analyses on optical-phonon-derived uniaxial negative thermal expansion system $Tr$Zr$_{2}$ ($Tr$ = Fe and Co$_{1-x}$Ni$_{x}$)

Pressure-induced volumetric negative thermal expansion in CoZr2 superconductor

Sign change in c-axis thermal expansion and lattice collapse by Ni substitution in Co1-xNixZr2 superconductors

Pressure‐Induced Volumetric Negative Thermal Expansion in CoZr2 Superconductor

Specific heat analyses on optical-phonon-derived uniaxial negative thermal expansion system TrZr2 (tr = fe and Co1− xNix)

Superconductivity of high-entropy-alloy-type transition-metal zirconide (Fe,Co,Ni,Cu,Ga)Zr2

Superconducting properties and electronic structure of CuAl2-type transition-metal zirconide Fe1-xNixZr2

Room Temperature Zero Thermal Expansion in a Cubic Cobaltite.

Anomalous Lattice Expansion of Bi-Based Superconductors

Giant negative thermal expansion in magnetic nanocrystals

Adjustable Magnetic Phase Transition Inducing Unusual Zero Thermal Expansion in Cubic RCo2-Based Intermetallic Compounds (R = Rare Earth)

Thermal Expansion Anomaly in High Tc La1.85Sr0.15CuO4 Associated with the Superconductivity

Interplanar Magnetic Orders and Symmetry-Tuned Zero Thermal Expansion in Kagomé Metal (Zr,Ta)Fe 2

Superconductivity in Non-Centrosymmetric ZrNiAl and HfRhSn-type Compounds.

Effect of Cobalt Doping on the Structural, Magnetic and Abnormal Thermal Expansion Properties of NaZn13-type La(Fe1-xCox)11.4Al1.6 Compounds.

Zero Thermal Expansion In Magnetic And Metallic Tb(Co,Fe)(2) Intermetallic Compounds