Enhanced Silicon PV efficiency by solar light spectral modulation via photonically tuned porphyrin‐iron oxide hybrid thin films

Mengyao Lyu,Jou Lin,Yuxin Wang,Ovais Aulakh,Nathan Ceja,Mary Sheryl Ramesh,Elisabeth Salazar,John Krupczak,Donglu Shi

DOI: https://doi.org/10.1002/ente.202300144

IF: 4.149

2023-03-27

Energy Technology

Abstract:The key challenge in photovoltaic solar applications has been the limitation of power conversion efficiency (PCE) as it is dictated by the intrinsic processes in a semiconductor. In particular, the temperature dependence of PCE needs to be addressed upon long‐term solar irradiation. In this study, we develop an alternative strategy by modulating the solar light spectrum with a series of photonic hybrids. Transparent thin films are synthesized with the solutions of porphyrin compounds and iron oxides which exhibit strong absorptions in the UV and IR regions. These spectral modulating thin films are photonically tuned via compositional optimization to absorb photons near 400 nm and above 1127 nm from solar spectrum to reduce thermalization and sub‐band‐gap absorption. These spectral modulators are applied in a particular configuration above a commercial silicon panel to partially filter the simulated solar light. The PCE of the silicon panel suffers a significant decrease due to temperature increase from 22.9 °C to 92.9 °C after 60 min solar irradiation, resulting in a PCE decrease from 25.1 % to 16.3 %. With the transparent spectral modulators, upon solar irradiation for 60 min, the maximum PCE has maintained at 20.5 %. The mechanisms of PCE enhancement are identified based on reduced thermalization and sub‐band‐gap absorption. As shown in this figure, a transparent spectral modulator (TSM) is placed under the solar simulator so that the light passes through it, shining on a silicon PV panel. These transparent spectral modulators are made of various porphyrin and iron oxide compounds with different absorption spectra. These spectral modulators can effectively modify the incoming solar light spectrum by retarding photons in certain frequency ranges to suppress IR heating and thermalization so that PCE can be further increased under prolonged solar irradiation. A portion of solar light is able to direcly shine on the PV panel surface in the patterned region marked in yellow for enhanced ISC, while the rest of the solarlight is to be modulated by TSM for reducing thermalization in the UV and heating in the IR regions in order to increase VOC. The area ratio of TSM film‐covered to the unconvered PV surface is optimized for maximum PCE and output power. This article is protected by copyright. All rights reserved.

energy & fuels