Abstract:Phase-pure epitaxial bismuth ferrite (BiFeO3, BFO) thin films with a homogeneous mixed-phase structure were synthesized on (001)-oriented lanthanum aluminate (LaAlO3, LAO) substrates using chemical solution deposition. The phase development of the BFO thin film and its leakage current characteristics have been systematically investigated as a function of thickness (number of spin-coated layers) and the heat treatment process (heating temperature and dwell time). The results show that the tetragonal-like (T′) phase fraction changes dramatically from 35% (45 nm thick single layer) to 10% (250 nm thick four-layer films). In a two-layer film (80 nm) configuration, the T′-phase fraction was further tuned. When annealing at 640 °C for 30 min, this mixed-phase BFO film, despite its high T′-phase fraction (28%), shows the lowest leakage current (<0.1 A/cm2 at <500 kV/cm), comparable to 200 nm pulsed laser deposition-grown pure R-BFO thin films. In contrast to the observed bulk-limited Ohmic or space-charge-limited-conduction (SCLC)-predominant mechanism in pure R′-phase and low T′-phase fraction BFO thin films, the high T′-phase fraction (∼28%) mixed-phase BFO film displays an interface-limited Schottky emission to an SCLC mechanism transition with increasing electric field.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaelm.0c00891?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaelm.0c00891</a>.Detailed deposition process for all bismuth ferrite thin films; representative AFM topography images; Raman spectra of multilayer BFO thin films; high-angle X-ray θ–2θ diffraction patterns; pole figures of representative BFO films; and PFM amplitude and phase images of thin films (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.0c00891/suppl_file/el0c00891_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Characterization of polycrystalline BiFeO3 films prepared by magnetic-field-assisted 90° off-axis pulsed laser deposition

Characterization of columnar BiFeO3 thick films prepared by magnetic field-assisted pulsed laser deposition

Room Temperature Ferroelectric, Ferromagnetic and Magnetoelectric Properties of Ba-Doped Bifeo3 Thin Films

Ferroelectric Polarization Induced Selective Growth of BiFeO3 Nanocrystals with a Remarkable Ferromagnetism

Pure phase BiFeO$_3$ thin films sputtered over Si: A new route towards high magnetization

Polarization screening-induced epitaxial growth and interfacial magnetism of BiFeO<sub>3</sub>/PbTiO<sub>3</sub>nanoplates

BiFeO3/La0.7Sr0.3MnO3 heterostructures deposited on Spark Plasma Sintered LaAlO3 Substrates

Magnetic and Structural Properties of BiFeO$_{3}$ Thin Films Grown Epitaxially on SrTiO$_{3}$/Si Substrates

Polarization screening-induced epitaxial growth and interfacial magnetism of BiFeO3/PbTiO3 heterostructures

Polarization Screening-Induced Epitaxial Growth and Interfacial Magnetism of BiFeO3/PbTiO3 Nanoplates

Synthesis And Ferroelectric Properties Of Bifeo3 Thin Films Grown By Sputtering

The hydrothermal synthesis and formation mechanism of single-crystalline perovskite BiFeO3 microplates with dominant (012) facets

Investigation of electronic, ferroelectric and local electrical conduction behavior of RF sputtered BiFeO3 thin films

Tuning Phase Fractions and Leakage Properties of Chemical Solution Deposition-Derived Mixed-Phase BiFeO 3 Thin Films

Effects of Chemical Fluctuations on Microstructures and Properties of Multiferroic Bifeo3 Thin Films

Structural, Magnetic, and Ferroelectric Properties of T-like Cobalt-Doped BiFeO3 Thin Films

Single-Crystal BiFeO3 Nanoplates with Robust Antiferromagnetism

Epitaxial Bi2FeCrO6 Multiferroic Thin Films

SYSTEMATIC EXPLORATION OF THE EFFECTS OF CR-DOPING ON MICROSTRUCTURE, INSULATING, AND FERROELECTRIC PROPERTIES OF BiFeO3 THIN FILM

Polarization Fatigue of Bifeo3 Films with Ferromagnetic Metallic Electrodes

Tetragonal BiFeO3 on Yttria-Stabilized Zirconia