Abstract:This study presents the alloy development of a new class of L12-strengthened Co-Al-Nb-based alloys with high γ′-solvus temperatures together with superb strengths at both ambient and elevated temperatures. The L12-Co3(Al, Nb) phase was found to be in equilibrium with the γ-Co matrix and the B2-CoAl phase in the ternary Co-10Al-3Nb alloy after an isothermal aging at 700 °C; however, it transformed into the Laves phase as the aging temperature increased to 800 °C. Alloying additions of Ni helped to suppress the B2 phase formation, resulting in a clean γ-γ′ dual-phase microstructure. Ti and Ta elements further stabilized the L12 structure and increased the γ′-solvus temperature to 1150 °C without inducing the formation of any other deleterious intermetallic phases. The newly developed Co-Al-Nb-Ni-Ti-Ta multicomponent Co-rich alloy has demonstrated outstanding yield strengths at both ambient and elevated temperatures, reaching 1023 ± 27 MPa at 25 °C and 897 ± 53 MPa at 700 °C, respectively. Furthermore, electron microscopy analyses uncovered unique deformation substructures, in which plasticity is predominantly carried out via nanoscale matrix-channel-confined stacking faults. As determined by the first-principle calculations, the absence of particle shearing upon deformation at ambient temperature is ascribed to the ultrahigh planar fault energies of the multicomponent γ′ precipitates. High-density superlattice-stacking-fault shearing and their interactions are responsible for the yield anomaly at 700 °C. These findings not only provide the fundamental understanding of the deformation behavior of the L12-strengthened alloys, but also demonstrate the great potential for developing next-generation high-temperature structural materials based on the multicomponent Co-rich alloy systems.

Formation of ternary L12 compounds in Al3Ti-base alloys

Orderly Nucleation and Competitive Growth Behaviors of Ti-Al Intermetallic Compounds in Ti/TiAl3 Diffusion Couple under High Temperature

The Mechanical Properties of Intermetallic Ni50−xTi50Alx Alloys (X=6,7,8,9)

TEM Characterization of Plate-Shaped L12-(Al,Ag)3Ti Precipitates in a Ag-modified TiAl Based Intermetallics

Phase Transformations of the L1 2 -Ti 3 Al Phase in Γ-Tial Alloy

Deformation and dislocation structure in L12 titanium trialuminide alloys

Ternary phases forming adjacent to Al3MnAl4Mn in AlMnTM (TM = Fe, Co, Ni, Cu, Zn, Pd)

Metastable state transformations of Al3Ti-base alloys during mechanical milling and subsequent annealing

Phase Stability and Precipitation in L12-Strengthened CoCrNi Medium-Entropy Alloys at Intermediate Temperatures

Role of (Al, Ti) alloying and annealing temperature in precipitation, recrystallization, and mechanical properties of ferrous multi-component alloys

Effect of Alloying Elements on the High-Temperature Yielding Behavior of Multicomponent γ'-L12 Alloys

The Role of In-Situ Al3Ti Formed During Solidification in Improving the High-Temperature Properties of Al-Cu Alloy

The precipitation reaction in a Ag-modified TiAl based intermetallic, as studied by TEM

Effect of Cr content on precipitation behavior of (CoCrNi)94Ti3Al3 medium entropy alloys

Grain-boundary Segregation and Superior Mechanical Properties in a Multicomponent L12 Ni46.5Co24Fe8Al12.5Ti9 Superlattice Alloy

First-principles Calculations of the Site Preference, Phase Stability and Brittle Versus Ductile Behaviors of TiAl Intermetallic Alloyed with Ternary Elements

Phase Constituents in Ni–Al–Co–Ti Quaternary Alloys

Effects of alloying elements on the atomic structure, elastic and thermodynamic properties of L12-Co3(V, Ti) compound

Multiphase Strengthening of Al3Ti-based Intermetallic Alloy

L12-strengthened Multicomponent Co-Al-Nb-based Alloys with High Strength and Matrix-Confined Stacking-Fault-mediated Plasticity

The Thermal Properties of L12 Phases in Aluminum Enhanced by Alloying Elements