Abstract:In this study, flame retardant polyurethane rigid foam was prepared by incorporating 15wt% ammonium polyphosphate (APP) and ionic liquid (1-butyl-2,3-dimethylimidazolium tetrafluoroborate, abbreviated as B 4 F). The flame retardant and thermal stability of the material were evaluated using vertical combustion (UL-94), limiting oxygen index (LOI), cone calorimeter (CONE), and thermogravimetric analyzer (TG) tests. Additionally, scanning electron microscopy (SEM), Raman spectroscopy (Raman), and X-ray photoelectron spectroscopy (XPS) were utilized to explore the flame retardancy mechanism in the carbon layer after combustion. The experimental results showed that the addition of 1wt%B 4 F to the flame-retardant polyurethane (RPUF/14APP/1B 4 F) significantly improved the vertical combustion test, upgrading it from the V-1 level to the V-0 level. This improvement was attributed to the increased degree of graphitization of the material, as evidenced by the reduced ratio of amorphous carbon to graphitic carbon (I D /I G ) from 2.68 to 1.38. XPS analysis revealed that RPUF/14APP/1B 4 F exhibited a higher C/O ratio in the residual carbon (3.03) compared to RPUF/15APP (1.84), indicating that B 4 F effectively enhanced the antioxidant properties of the flame-retardant materials. Under the air atmosphere, RPUF/14APP/1B 4 F demonstrated an increased char formation at 800 °C (21.24%), which was 71.01% higher than RPUF/15APP. The interaction between B 4 F and APP led to the formation of a more stable char layer structure in polyurethane, further enhancing its flame retardancy. In conclusion, the RPUF/14APP/1B 4 F demonstrated a synergistic flame retardancy effect and enhanced thermal stability. The addition of B 4 F improved the graphitization degree of the material and increased the C/O ratio in the residual carbon, enhancing the antioxidant properties of the system. Moreover, the interaction between B 4 F and APP promoted the formation of a more stable char layer, effectively improving the flame retardant properties of the polyurethane. These findings provide valuable insights for the development of advanced flame retardant polyurethane materials with improved fire safety in various applications.

Effect of ammonium polyphosphate on flame retardancy of bio-based rigid polyurethane foams

Fabrication of Flame-Retardant Ammonium Polyphosphate Modified Phytic Acid-Based Rigid Polyurethane Foam with Enhanced Mechanical Properties

Ammonium Polyphosphate Modified with Β-Cyclodextrin Crosslinking Rigid Polyurethane Foam: Enhancing Thermal Stability and Suppressing Flame Spread

Effect of ammonium polyphosphate/cobalt phytate system on flame retardancy and smoke & toxicity suppression of rigid polyurethane foam composites

Lignin-derived Core-Shell Flame Retardants for Fire-Safety Rigid Polyurethane (RPU) Insulations

Functionalized Lignin for Halogen-Free Flame Retardant Rigid Polyurethane Foam: Preparation, Thermal Stability, Fire Performance and Mechanical Properties

Analysis of the Pyrolysis Process of Ionic Liquid-Based Flame Retardant Rigid Polyurethane Foam

Highly Efficient Flame Retardancy and Fire Spread Behavior of Rigid Polyurethane Foams with extremely low content of Flame Retardant

Study on the Flame Retardant Properties of Microcapsule Ammonium Polyphosphate Polyurethane Rigid Foam

Bio-Based Alkali Lignin Cooperative Systems for Improving the Flame Retardant and Mechanical Properties of Rigid Polyurethane Foam

Effects Of Expandable Graphite And Ammonium Polyphosphate On The Flame-Retardant And Mechanical Properties Of Rigid Polyurethane Foams

Roles of Organically-Modified Montmorillonite and Phosphorous Flame Retardant During the Combustion of Rigid Polyurethane Foam

Acoustic Performance and Flame Retardancy of Ammonium Polyphosphate/Diethyl Ethylphosphonate Rigid Polyurethane Foams

Surface-modified ammonium polyphosphate for flame-retardant and reinforced polyurethane composites

Preparation of melamine–formaldehyde resin-microencapsulated ammonium polyphosphate and its application in flame retardant rigid polyurethane foam composites

Improved thermal stability and flame retardancy of soybean oil-based polyol rigid polyurethane foams modified with magnesium borate hydroxide and ammonium polyphosphate

THERMAL DEGRADATION AND SMOKE PRODUCTION DURING COMBUSTION FOR INTUMESCENT FLAME RETARDANT RIGID POLYURETHANE FOAMS

Aluminum Hypophosphite in Combination with Expandable Graphite As A Novel Flame Retardant System for Rigid Polyurethane Foams

Green flame-retardant rigid polyurethane foam with cobalt hydroxystannate to improve the thermal stability, flame retardancy and smoke suppression properties

Study on the Flame Retardancy of Rigid Polyurethane Foam with Phytic Acid-Functionalized Graphene Oxide

Combustion and Thermal Properties of Flame Retardant Polyurethane Foam With Ammonium Polyphosphate Synergized by Phosphomolybdic Acid