Effect of the Cu additives on strain-induced coarsening of the Laves phase in Re-containing 10% Cr–3% Co martensitic steels

A. Fedoseeva,A. Klauz,N. Iskandarov,A. Boev,D. Aksyonov,R. Kaibyshev

DOI: https://doi.org/10.1016/j.msea.2024.146306

2024-02-01

Abstract:The effect of the Cu additives (0.8 wt%) on strain-induced coarsening of the Laves phase was investigated via the comparison of the Laves phase behavior in the Re-containing steels with the different W and Cu contents during creep and aging at a temperature of 650 °C. The formation of the “Cu”-clusters/precipitates with an average size of 3 nm randomly distributed within the ferritic matrix was revealed in the steel with 0.8% Cu, which gave +(20–50) MPa to the room yield strength compared to the steels with 0.2% Cu. The strengthening mechanism due to the “Cu”-clusters/precipitates was revealed as a linear sum of the chemical effect induced by the creation of a new interface area during the cutting of the dislocation through the particle and the pinning of the glide dislocation by an array of obstacles. During creep and aging, the fine “Cu”-clusters/precipitates were dissolved with the precipitation of the fcc “Cu”-rich phase along the boundaries. The nucleation of the Laves phase on the fcc “Cu”-rich phase along the boundaries was detected, which provided the increase in particle number density during both aging and creep conditions. During aging, the coarsening rate constant of the Laves phase particles in the steel with 0.8% Cu was minimal among all studied steels that was caused by the Cu atoms occupying the favorable positions for segregation along the boundaries. However, during creep, the Laves phase also nucleated on the “Cu”-clusters/precipitates, which led to abnormal precipitation of the Laves phase within the martensitic laths and the accelerated growth of the grain boundary Laves phase particles. The grain boundary Laves phase demonstrated intensive strain-induced coarsening during creep, increasing the value of the coarsening rate constant by one order of magnitude compared to the aged state. This is related to the initiation of the additional diffusion way of W atoms from the Laves phase located within the lath interiors to the grain boundary particles.

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering