Electrochemically Anodized V 2 O 5 as an Efficient Sodium Cathode

Lin Wang,Yichun Wang,Anmin Cao,Jiangfeng Ni,Liang Li

DOI: https://doi.org/10.1021/acs.energyfuels.1c00438

2021-04-26

Abstract:Vanadium oxide has a high theoretical capability for sodium storage, but this capability has often been plagued by sluggish electrochemical reaction kinetics upon sodiation/desodiation. To alleviate this problem, we report on an ordered structure of V₂O₅ nanopores by electrochemical anodization. The nanopores are amorphous in structure, 30–40 nm in diameter, and ∼2.4 μm in depth, exhibiting favorable electrochemical performance for sodium. In the potential range between 1.5 and 3.8 V, the nanoporous architecture of V₂O₅ displays a reversible capacity of 177 mAh g^–1 with initial coulombic efficiency of 74% and retains a capacity of 69 mAh g^–1 over 50 cycles at a higher rate of 100 mA g^–1. The open framework of nanopores and the isotropic properties of the amorphous structure are believed to be responsible for the appealing electrochemical performance of anodized V₂O₅.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.1c00438?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.1c00438</a>.SEM images of various V₂O₅ films (Figure S1), XRD and charge–discharge curves of annealed V₂O₅ (Figure S2), and performance comparison of V₂O₅ cathodes (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.1c00438/suppl_file/ef1c00438_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

energy & fuels,engineering, chemical

What problem does this paper attempt to address?

The paper primarily focuses on the key material in sodium-ion battery technology—vanadium pentoxide (V₂O₅), aiming to address the issues of structural instability and slow electrochemical reaction kinetics when V₂O₅ is used as a cathode material for sodium-ion batteries.

Specifically, the researchers prepared V₂O₅ films with nanoporous structures through electrochemical anodization. This nanoporous structure not only increases the specific surface area of the material, which is beneficial for enhancing electrochemical performance, but its amorphous nature also helps improve the diffusion rate of sodium ions during the charge-discharge process. Experimental results show that within the voltage range of 1.5 to 3.8 volts, this nanoporous V₂O₅ cathode material can exhibit good reversible capacity (up to 177mAh/g under initial coulombic efficiency) as well as high cycling stability and rate performance. After 50 cycles, it can still maintain a capacity of 69mAh/g at a high current density of 100mA/g.

Therefore, the method proposed in this paper effectively addresses the challenges faced by V₂O₅ as a cathode material for sodium-ion batteries and demonstrates excellent electrochemical performance, providing new insights for the development of sodium-ion batteries.