Fabrication of a Sandwiched Core Carbon Sphere@Na 3 V 2 (PO 4 ) 2 O 2 F@N-Doped Carbon Cathode for Superior Sodium-Ion Batteries
Yi Zhu,Enze Xu,Jiamin Zhang,Junjie Quan,Hui Wang,Zhenjie Sun,Yang Jiang
DOI: https://doi.org/10.1021/acsaem.1c00334
IF: 6.4
2021-03-18
ACS Applied Energy Materials
Abstract:Cathode materials play a decisive role in the building of high energy density sodium-ion batteries. Among them, Na<sub>3</sub>V<sub>2</sub>(PO<sub>4</sub>)<sub>2</sub>O<sub>2</sub>F (NVPOF) is receiving active attention due to its high structural integrity, satisfactory work voltage, and outstanding energy density. However, its practical application is still impeded by the poor rate performance related to its low intrinsic electronic conductivity. Herein, Na<sub>3</sub>V<sub>2</sub>(PO<sub>4</sub>)<sub>2</sub>O<sub>2</sub>F grown on the surface of the core carbon sphere () was initially synthesized via a one-step hydrothermal method. Subsequently, by carbonization of polydopamine, the above particles coated with a uniform N-doped carbon layer (@NC) were successfully fabricated. This sandwiched structure built by a core carbon sphere and carbon layer can significantly improve the electronic conductivity, boost sodium-ion diffusion kinetics, and mitigate volume change of the electrode upon the cycling process. As a result, the as-prepared electrode exhibits a desirable specific capacity of 119.8 mA h g<sup>–1</sup> with an attractive capacity retention of 96% after 100 cycles at a current density of 1 C. Even at a high current density of 10 C, the capacity can retain 103.9 mA h g<sup>–1</sup>, and the capacity decay per cycle is only 0.032% during 500 cycles, indicating outstanding electrochemical performance. All the analyses demonstrate that @NC has enormous potential as an applicable cathode for sodium-ion batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.1c00334?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.1c00334</a>.Computational methods, the microstructure of p-NVPOF, Raman spectrum and carbon content of and @NC, XRD patterns of different samples, CV curves of p-NVPOF and at a scan rate of 0.1 mV s<sup>–1</sup>, charge/discharge curves of p-NVPOF and at a current density of 1 C, charge/discharge curves of @NC at different current densities, the microstructure of @NC at a current density of 10 C after 500 cycles, rate performance of and p-NVPOF, impedance parameters for the equivalent circuits, and the reported Na<sub>3</sub>V<sub>2</sub>O<sub>2–2<i>x</i></sub>(PO<sub>4</sub>)<sub>2</sub>F<sub>1+2<i>x</i></sub> materials in the literature (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.1c00334/suppl_file/ae1c00334_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels