Abstract:Electrolytic manganese residue (EMR) is a solid waste that contains a significant amount of soluble manganese and ammonia nitrogen, which can pose risks to human health if improperly disposed of. This study aimed to prepare cementitious materials containing abundant ettringite crystals by mixing EMR with various proportions of granulated blast furnace slag (GBFS) and alkaline activators (CaO, Ca(OH) 2 , clinker, NaOH). The resulting cementitious material not only utilized a substantial amount of EMR but also exhibited comparable strength to ordinary Portland cement. The optimal ratios were determined through mechanical testing. Additionally, the leaching toxicity of cementitious materials was assessed using ICP-MS (inductively coupled plasma mass spectrometer) tests. The microscopic properties, hydration, and mechanism of heavy metal solidification in the cementitious materials were evaluated using XRD (X-ray diffraction), SEM (scanning electron microscope), EDS (energy-dispersive spectrometer), FTIR (Fourier transform infrared spectroscopy), and TG (thermogravimetric) techniques. The results showed that the optimal ratio for the cementitious materials was 60% EMR, 36% GBFS, and 4% Ca(OH) 2 . The hardened mortar exhibited compressive strengths of 34.43 MPa, 41.3 MPa, and 50.89 MPa at 3 days, 7 days, and 28 days, respectively, with an EMR utilization rate of 60%. The hydration products of EMR-based cementitious materials were C-(A)-S-H, AFt, and ferromanganese compounds, which contribute to the mechanical strength. The Mn 2+ and NH 4 + -N contents of raw EMR were 1220 and 149 mg/L, respectively. Nonetheless, the leaching of Mn 2+ and NH 4 + -N in the alkali-EMR-GBFS system was significantly below the limits set by the Chinese emission standard GB8978-1996. Within this system, C-(A)-S-H and AFt could physically adsorb and displace heavy metals, Ca 6 Mn 2 (SO 4 ) 2 (SO 3 ) 2 (OH) 12 · 24H 2 O could replace Al ions with Mn ions, and ferromanganese compounds Fe 2 Mn(PO 4 ) 2 (OH) 2 · (H 2 O) 8 and MnFe 2 O 4 could chemically precipitate Mn 2+ .

Characteristic contaminant removal purification and high value ecological utilization technology of calcination modified manganese residue

Research Status and Environmental Protection Disposal of Recycled Electrolytic Manganese Residue

Reuse of hazardous electrolytic manganese residue: Detailed leaching characterization and novel application as a cementitious material

Study of microscopic properties and heavy metal solidification mechanism of electrolytic manganese residue-based cementitious materials

Utilizing desulphurized electrolytic-manganese residue as a mineral admixture: A feasibility study

Study on the mechanism and mechanical properties of magnesium oxychloride cement for blocking pollutants migration from electrolytic manganese residue

Study on the Performance and Mechanism of Cement Solidified Desulfurization Manganese Residue

Mechanical properties and environmental characteristics of the synergistic preparation of cementitious materials using electrolytic manganese residue, steel slag, and blast furnace slag

Harmless treatment of electrolytic manganese residue: Ammonia nitrogen recovery, preparation of struvite and nonsintered bricks

An innovative method for manganese (Mn2+) and ammonia nitrogen (NH4+-N) stabilization/solidification in electrolytic manganese residue by basic burning raw material

Hazard-Free Treatment of Electrolytic Manganese Residue and Recovery of High-Concentration SO2 Using High-Temperature Reduction Roasting Process

Insight into mechanisms of Mn and NH 4 + -N removal with recovery of Mn and Mg from electrolysis manganese residue (EMR): Effect of humus and NaOH

Effect of Electrolytic Manganese Residue in Fly Ash-Based Cementitious Material: Hydration Behavior and Microstructure

Progress in comprehensive utilization of electrolytic manganese residue: a review

Study on the leaching toxicity and performance of manganese slag-based cementitious materials

Study on mutual harmless treatment of electrolytic manganese residue and red mud

Innovative Techniques for Electrolytic Manganese Residue Utilization: A Review

Study on harmless treatment of electrolytic manganese residue by low temperature thermochemical method

Ammonia removal and simultaneous immobilization of manganese and magnesium from electrolytic manganese residue by a low-temperature CaO roasting process

Preparation of activated electrolytic manganese residue-slag-cement ternary blended cementitious material: Hydration characteristics and carbon reduction potential

Highly efficient Mn2+, Mg2+, and NH4+ recovery from electrolytic manganese residue via leaching, solvent extraction, coprecipitation, and atmospheric oxidation