The effects of synthesis route and LaB 6 -doping on FeCoNiCrTi coating performance: Morphology, microstructure, microhardness and corrosion resistance

Dadong Jie,Meiping Wu,Rui He,Chen Cui,Yuling Gong,Xiaojin Miao
DOI: https://doi.org/10.1016/j.optlastec.2024.110747
IF: 4.939
2024-02-24
Optics & Laser Technology
Abstract:In this work, the FeCoNiCrTi HEA coatings were fabricated on the Ti6Al4V surface via laser cladding technology. The effects of synthesis routes (different energy density, L ed ) and LaB 6 -doping on the single-track morphology, phase distribution, microstructure, microhardness and corrosion resistance of HEA coatings were comprehensively studied. Interestingly, the regulation of L ed and addition of LaB 6 significantly reduced the crack sensitivity and dilution rate of the coating. On the one hand, the optimized coating contributed to fine grain size when L ed was 73.33 J/mm 2 . On the other hand, the in-situ generation of TiC, TiB 2 and TiC/TiB 2 composite structure played an important role in achieving the more excellent propertiy in LaB 6 /FeCoNiCrTi composite coating. Furthermore, the microhardness and corrosion resistance of the coatings were significantly improved owing to the ceramic phases and fine grain strengthening. Specifically, the average microhardness coating was up to 593 HV 0.2 . The corrosion current density ( I corr ) of the coating with a L ed of 73.33 J/mm 2 was 4.796 × 10 −6 A · cm −2 , the carrier density (N D ) and thickness ( d ) of the passivation film were 1.556 × 10 22 cm −2 and 3.244 nm, respectively, indicating the best corrosion resistance in HEA coatings. In terms of LaB 6 /FeCoNiCrTi coating, the I corr , N D and d were 2.400 × 10 −6 A·cm −2 , 1.053 × 10 22 cm −2 and 4.739 nm, respectively. Consequently, the doping of LaB 6 further enhanced the corrosion resistance of HEA coating.
optics,physics, applied
What problem does this paper attempt to address?