Hydrogen Permeation Behavior of 45 Steel during Zinc Nickel Alloy Electroplating and Hydrogen Embrittlement Susceptibility of the Electroplated Coating

Lin Xi-hu

Abstract:Double-electrolysis-cell hydrogen-monitoring method was adopted to investigate the hydrogen permeation behavior of 45 steel during Zn-Ni alloy electroplating under different temperature,current density and bath pH value.In the meantime,tensile tests at a slow-strain-rate were conducted to evaluate the hydrogen embrittlement susceptibility of the electroplated coating.Furthermore,the morphology of the fractured surface of the electroplated coating was examined with a scanning electron microscope.Results indicated that the electroplating bath temperature had the most significant effect on the hydrogen permeation current.The fractured time of as-plated steel tended to decrease with elevating bath temperature,and the hydrogen embrittlement susceptibility of the electroplated coating tended to rise therewith.Besides,as-plated steel sample had shorter fractured time than the blank sample,which indicated that the former had higher hydrogen embrittlement susceptibility.Moreover,as-plated steel sample was dominated by cleavage fracture,while the blank counterpart was dominated by tough fracture.In one word,the hydrogen embrittlement susceptibility of electroplated Zn-Ni alloy coating could be indirectly evaluated by using hydrogen permeation current curve.

Engineering,Materials Science