Abstract:In order to study the durability of concrete materials subjected to sulfate attack, in a sulfate attack environment, a series of concrete tests considering different fly ash contents and erosion times were conducted. The mechanical properties and the micro-structure of concrete under sulfate attack were studied based on the following: uniaxial compressive strength test, split tensile test, ultrasonic impulse method, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The mechanical properties were compressive strength, splitting tensile strength, and relative dynamic elastic modulus, respectively. Additionally, according to the damage mechanical theory, experimental results and micro-structure analysis, the damage evolution process of concrete under a sulfate attack environment were studied in detail. Finally, according to the sulfate attack time and fly ash content, a damage model of the sulfate attack of the binary surface was established. The specific results are as follows: under the action of sulfate attack, the change law of the rate of mass change, relative dynamic modulus of elasticity, corrosion resistance coefficient of compressive strength, and the corrosion resistance coefficient of the splitting tensile strength of concrete all increase first and then decrease. Under the same erosion time, concrete mixed with 10% fly ash content has the best sulfate resistance. Through data regression, the damage evolution equation of the sulfate attack was developed and there is an exponential function relationship among the different damage variables. The binary curved surface regression effect of the concrete damage and the erosion time and the amount of fly ash is significant, which can predict deterioration of concrete damage under sulfate attack. During the erosion time, the combined expansion of ettringite and gypsum caused micro cracks. With an increase of corrosion time, micro cracks developed and their numbers increased.

Electrochemical investigation of accelerated deterioration of concrete with iron-sulfide containing aggregates

Corrosion-Induced Cracking Propagation Of Rc Beams Subjected To Different Corrosion Methods And Load Levels

Developing a Novel Expression for Chloride Ion Concentration Threshold in Reinforced Concrete: Integration of Electrochemical Analysis and Time-Dependent Modeling

Corrosion of Steel Embedded in Mortar and Concrete under Different Electrolytic Accelerated Corrosion Methods

Applicability Study on Accelerated Corrosion Methods of Steel Bars in Concrete Structure

Multi-phase Modelling of Electrochemical Rehabilitation for ASR and Chloride Affected Concrete Composites

Dynamic Self-Balanced Electrochemical Model for Non-Uniform Corrosion of Steel Reinforcement in Concrete under Combined Effects of Heat-Moisture-chlorine-oxygen

Experimental study on electrical characteristics of ions in concrete at early age under electric field

A new accelerated testing scheme to evaluate the potential oxidation reaction of sulfide-bearing aggregates in concrete specimens

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Accelerating Tests For The Performance Deterioration Of Concrete Exposed To Chloride Media

Preparation of concrete specimen for internal sulfate attack analysis using electron backscatter diffraction

Degradation Mechanisms of Chloride Contaminated Cast-in-Situ Concrete Partially Exposed to Magnesium-Sulfate Combined Environment

Damage Evolution of Concrete under the Actions of Stray Current and Sulphate

The Electrochemical Characterization of Rebar Passivation Film in Simulated Concrete Media

Exploratory Study on Sulfate Attack Monitoring of Concrete Structures Using Piezoceramic Based Smart Aggregates

Concrete Deterioration Mechanisms under Combined Sulfate Attack and Flexural Loading

Mechanical Properties and Damage Evolution of Concrete Materials Considering Sulfate Attack

Effect of an Early-Age Exposure on the Degradation Mechanisms of Cement Paste under External Sulfate Attack

Study on the Deterioration of Concrete under Dry-Wet Cycle and Sulfate Attack

Partially-exposed cast-in-situ concrete degradation induced by internal-external sulfate and magnesium multiple coupled attack