PN Heterostructure Interface-Facilitated Proton Conduction in 3C-SiC/Na 0.6 CoO 2 Electrolyte for Fuel Cell Application
Faze Wang,Yueming Xing,Enyi Hu,Jun Wang,Jing Shi,Sining Yun,Bin Zhu
DOI: https://doi.org/10.1021/acsaem.1c01633
IF: 6.4
2021-08-12
ACS Applied Energy Materials
Abstract:Cubic SiC is one of the emerging semiconductors utilized in power and electronic devices. In this work, 3C-SiC was tuned to protonic conducting properties via constructing an n–p heterostructure composite with Na0.6CoO2 (NCO). The peak power density of the fuel cell with 1:1.5 3C-SiC/NCO as an electrolyte is 251.6 mW cm–2, while its corresponding ionic conductivity reaches 0.12 S cm−1 at 550 °C. The band alignment and local electric field at the interface are simulated to explain the 3C-SiC/NCO conducting mechanism and device electrochemical performances. This research indicates that 3C-SiC can be modulated to proton conducting material through a semiconductor heterostructure interface mechanism.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsaem.1c01633.Experiment method, TEM and SEM images (Figures S1 and S2), IV-IP curves and EIS spectrum (Figures S3 and S4), O 1S XPS spectra (Figure S5), UPS and UV–vis results (Figure S6), simulated results from EIS spectra (Table S1), and XPS data, showing peak assignment, area, and atomic concentration (Table S2) (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,energy & fuels