Abstract:The InGaN films and GaN/InGaN/GaN tunnel junctions (TJs) were grown on GaN templates with plasma-assisted molecular beam epitaxy. As the In content increases, the quality of InGaN films grown on GaN templates decreases and the surface roughness of the samples increases. V-pits and trench defects were not found in the AFM images. p ++ -GaN/InGaN/n ++ -GaN TJs were investigated for various In content, InGaN thicknesses and doping concentration in the InGaN insert layer. The InGaN insert layer can promote good interband tunneling in GaN/InGaN/GaN TJ and significantly reduce operating voltage when doping is sufficiently high. The current density increases with increasing In content for the 3 nm InGaN insert layer, which is achieved by reducing the depletion zone width and the height of the potential barrier. At a forward current density of 500 A/cm 2 , the measured voltage was 4.31 V and the differential resistance was measured to be 3.75 × 10 −3 Ω·cm 2 for the device with a 3 nm p ++ -In 0.35 Ga 0.65 N insert layer. When the thickness of the In 0.35 Ga 0.65 N layer is closer to the "balanced" thickness, the TJ current density is higher. If the thickness is too high or too low, the width of the depletion zone will increase and the current density will decrease. The undoped InGaN layer has a better performance than n-type doping in the TJ. Polarization-engineered tunnel junctions can enhance the functionality and performance of electronic and optoelectronic devices.

Tunneling assisted p-contact free GaN-InGaN green light-emitting diodes

n+/p+ GaN and n+/p+ Al0.10Ga0.90N tunnel junctions: a promising alternative for hole injection in deep ultraviolet light-emitting diodes

Improvement of Blue Llight-Ight-ight-eeemitting Mitting Ddiodes Iodes with an Undoped Graded Layer As the Electrons Tunneling Barrier Layer

Graphene/p-AlGaN/p-GaN Electron Tunnelling Light Emitting Diodes with High External Quantum Efficiency

Advantages of AlGaN Tunnel Junction in N-Polar 284nm Ultraviolet-B Light Emitting Diode

Performance evaluation of tunnel junction-based N-polar AlGaN deep-ultraviolet light-emitting diodes

Hybrid Tunnel Junction–Graphene Transparent Conductive Electrodes for Nitride Lateral Light Emitting Diodes

High-efficiency Green Micro-Leds with GaN Tunnel Junctions Grown Hybrid by PA-MBE and MOCVD

Non-heavy doped pnp-AlGaN tunnel junction for an efficient deep-ultraviolet light emitting diode with low conduction voltage

Recent Progress in III‐Nitride Tunnel Junction Light‐Emitting Diodes

Performance-boosted N-polar AlGaN Deep Ultraviolet Light-Emitting Diodes by a Top Tunnel Junction

Electrical properties and structural optimization of GaN/InGaN/GaN tunnel junctions grown by molecular beam epitaxy

Design of AlInAs/InP Tunnel Junction and Its Application in Devices

Demonstration of N-Polar III-Nitride Tunnel Junction LED

Efficient AlGaN-Based Deep-Ultraviolet LED with N-Side Located Tunnel Junction

Calculating the Effect of AlGaN Dielectric Layers in a Polarization Tunnel Junction on the Performance of AlGaN-Based Deep-Ultraviolet Light-Emitting Diodes

High internal quantum efficiency of green GaN-based light-emitting diodes by thickness-graded last well/last barrier and composition-graded electron blocking layer

Enhanced Light Extraction from a GaN-based Green Light-Emitting Diode with Hemicylindrical Linear Grating Structure.

Activation of buried p-GaN through nanopipes in large-size GaN-based tunnel junction LEDs

GdN Nanoisland-Based GaN Tunnel Junctions

Study on Optical Properties and Internal Quantum Efficiency Measurement of GaN-based Green LEDs