The Hot Ductility, Microstructures, Mechanical Properties and Corrosion Resistance in an Advanced Boron-Containing Complex Phase Steel Heat-Treated Using the Quenching and Partitioning (Q&P) Process
Antonio Enrique Salas-Reyes,Gerardo Altamirano-Guerrero,Rogelio Deaquino,Armando Salinas,Gabriel Lara-Rodriguez,Ignacio Alejandro Figueroa,Jesús Rafael González-Parra,Barrie Mintz
DOI: https://doi.org/10.3390/met13020257
IF: 2.695
2023-01-29
Metals
Abstract:The objective of this research work is to obtain the hot ductility behavior, and the structural, microstructural and mechanical characteristics of one of the latest generation of AHSS steels, a complex phase (CP) steel microalloyed with boron (0.006 wt.%), processed by hot and cold rolling operations and heat-treated using two different quenching and partitioning (Q&P) treatments, a one-step partitioning (quenching to 420 °C) and the other a two-step partitioning (quenching to 420 °C and reheated to 600 °C). The results show that boron has a marked effect on the solidification process of the CP steel, refining the austenitic grain size. Due to its refinement, the boron-containing steel had better ductility throughout the temperature range examined (700–900 °C), i.e., the hot ductility trough. Thus, the minimum percentage of reduction in area (%RA) value occurring at 800 °C was 43% for the boron-free steel, compared with 58% for the boron-containing steel. Hence, cracking would not be a problem when straightening the strand on continuous casting. The benefit of boron addition on the room temperature properties was found to be very marked for the higher temperature two-step partitioning treatment, giving a yield stress of 1200 MPa, a UTS (ultimate tensile strength) of 1590 MPa and a total elongation above 11%. The final Q&P microstructure, in both one- and two-step partitioning conditions, consisted of retained austenite (RA-γ), martensite and ferrite islands in a bainitic matrix. Furthermore, the boron treated steel on quenching produced a greater amount of RA-γ, which accounted for its better room temperature ductility and produced a martensitic matrix rather than a bainitic one, giving it greater strength. The addition of boron improved the corrosion resistance of this type of third generation AHSS steel.
materials science, multidisciplinary,metallurgy & metallurgical engineering