Abstract:<p>High borated steel sheets containing 0.25 wt% to 4.0 wt% boron including hypoeutectic (0.28 wt% B and 2.11 wt% B), eutectic (2.43 wt% B) and hypereutectic (4.01 wt% B) compositions were tried to be fabricated by a novel strip casting technology, and the effects of boron content on sub-rapid solidification behavior and subsequent microstructural evolution together with mechanical properties was studied. It was found that the morphology of borides depended greatly on the boron content. When increasing boron, the morphological change of borides was network-like → grainy → cluster-like → plate-like. Various orientation relationships between different morphological borides and γ-Fe in as-cast steels were also identified. After subsequent hot-rolling and solution-treating, ultra-fine (<10 μm) borides were obtained in hypoeutectic and eutectic steels. Benefiting from that, excellent mechanical properties was achieved, which was much better than that of steels prepared by traditional ingot casting. Particularly, when the boron content approached eutectic composition, of which the effect on the microstructure and mechanical properties was more sensitive. The steels containing 2.11 wt% and 2.43 wt% boron exhibited different morphological borides with a total elongation of 14.1% and 8.0%, respectively. Moreover, a thin hypereutectic borated steel sheet was also prepared, but the borides were very large and the total elongation was very low. The correlation between microstructure and strength was clarified based on the Hall-Petch behavior and intermetallic strengthening effect. Smaller γ-grains and higher volume fraction of borides were responsible for higher strength. The plastic behavior of steels was influenced by strain-hardening rate that was determined by the volume fraction of γ-Fe matrix. A better sustainable strain-hardening capability was beneficial to extend the stage of uniform deformation and enhance the ductility. In addition, the mechanical properties of steels were also decided by the fracture mechanism that was dominated by the size of borides.</p>

Mechanical and microstructure properties of ultra-high strength boron steel using rapid resistance heating without soaking

Experiment study on die quenching effect for ultra-high strength boron steel

Effect of Heat Treatment on Microstructures and Mechanical Properties of Al-Modified Boron High Speed Steel

The Effect of Quenching and Partitioning (Q&P) Heat Treatment on the Microstructure and Mechanical Properties of High Boron Steel

Flow behavior of boron steel for hot stamping at elevated temperature

Flow Behavior of Ultra-High Strength Boron Steel at Elevated Temperature

Fractional Cooling Strategy of the Hot-Stamping Process and Its Influence on Formability and Mechanical Properties of Ultra-High-Strength Steel Parts

Hot Stamping Processing Experiments of Quenchable Boron Steel

A Study of Heat Treatment of High‐boron High‐speed Steel Roll

The effect of ultra-fast surface hardening and strengthening on microstructure and mechanical properties of cast (9Cr–3Co–3W) heat-resistant steel

Effect of Deformation on Microstructure and Properties of Hot Stamping Boron Steel B1500HS

The Hot Ductility, Microstructures, Mechanical Properties and Corrosion Resistance in an Advanced Boron-Containing Complex Phase Steel Heat-Treated Using the Quenching and Partitioning (Q&P) Process

Microstructure and properties of high boron bearing steel

Experimental Study on Thermodynamic Performance of Boron Steel B1500HS Used for Hot Stamping Process

Effect of Heat Treatment on Microstructure and Property of High Boron and Low Carbon Cast Steel

Effect of Heat Treatment on Structure and Wear Resistance of High Chromium Cast Steel Containing Boron

Study on Surface Quality Analysis of an Uncoated Boron Steel and Its Oxide Layer Suppression Method for Hot Stamping

Experiments and Numerical Simulation of Hot Bending and Die Quenching for Ultra-High Strength Boron Steel

Effect of Heat Treatment Temperature on Microstructure and Properties of PM Borated Stainless Steel Prepared by Hot Isostatic Pressing

Effects of boron content on the microstructure and mechanical properties of twin-roll strip casting borated steel sheets

Effect of Quenching Temperature on Microstructure of High-Boron High Speed Steel