Abstract:As an innovative and promising BF iron-bearing burden, the vanadium-titanium magnetite carbon composite briquette (VTM-CCB) charging significantly affects the softening-melting-dripping characteristics and cohesive zone of the mixed burden. In this study, the interface behaviors between VTM-CCB and sinter were investigated by conducting interrupted softening-melting experiments to elucidate intrinsic structure evolution and interaction mechanisms. During softening, when the FC/O ratio of VTM-CCB ranges from 0.8 to 1.0, the molten slag-metal coexisting structure formed at the interface, thereby promoting the shrinking and decreasing T4 and T40. However, with increasing FC/O ratio higher than 1.0, the interface slagging and bonding would be suppressed due to the unconsumed carbon particles. During melting, the increasing of FC/O ratio would lower the FeO content and decrease the molten slag, and the interface layer transformed from molten slag-iron coexisting structure to dense metallic iron shell, suppressing the collapse of molten mixtures and increasing Ts. In the dripping process, increasing the FC/O ratio appropriately could promote the interface iron carburization and the aggregation of molten iron, thereby decreasing TD and improving the dripping performance. Besides, the VTM-CCB, acting as skeleton in the molten mixtures, could provide more gas channels to improve the permeability of packed bed. However, as the FC/O ratio exceeds 1.2, the Ti(C,N) would precipitate at the slag-metal interface and deteriorate the fluidity of molten mixtures, thereby deteriorating the gas permeability and increasing TD notably. Fully considering the softening-melting-dripping characteristics and the gas permeability, the appropriate FC/O ratio of VTM-CCB should not be higher than 1.2.

Interface behavior and oxidation consolidation mechanism of titanium-bearing iron sand particles with ball-milling pretreatment

Fundamental Study on Utilization of Titanium Resources by RHF Process

Research on the process and mechanism of preparing titanium-rich materials from complex ilmenite

Preparation, Sintering Behavior and Consolidation Mechanism of Vanadium-Titanium Magnetite Pellets

Interface Behavior and Interaction Mechanism between Vanadium-Titanium Magnetite Carbon Composite Briquette and Sinter in Softening-Melting-Dripping Process

Study on Influencing Factors of High-Temperature Basic Characteristics of Iron Ore Powder and Optimization of Ore Blending

Improvement of roasting and metallurgical properties of fluorine-bearing iron concentrate pellets

Effect of MgO Addition on the Metallurgical Properties of the Vanadium-Titanium Pellet with Simulating Blast Furnace Conditions

Combined Effect of SiO2 and O2 on the Crystallization Behavior of Modified Ti-Bearing Blast Furnace Slag

Effect of Titanomagnetite Ironsand Coal Composite Hot Briquette on Softening-melting Performance of Mixed Burden under Simulated Blast Furnace Conditions

The Preparation and Dust Suppression Performance Evaluation of Iron Ore Tailing-Based Cementitious Composites

Effect of diboron trioxide on the crushing strength and smelting mechanism of high-chromium vanadium–titanium magnetite pellets

Precipitation Behaviour of Ti Enriched Phase in Ti Bearing Slag

Titanium Impurity Control in V-Bearing Pig Iron Prepared via the Sodium Smelting of Vanadium–Titanium Magnetite

Co-modification and Crystalline-control of Ti-bearing Blast Furnace Slags

Fusion Separation of Vanadium-Titanium Magnetite and Enrichment Test of Ti Element in Slag

Effect of titanium on the sticking of pellets based on hydrogen metallurgy shaft furnace: Behavior analysis and mechanism evolution

Effect of Na2SO4 on the Embedding Direct Reduction of Beach Titanomagnetite and the Separation of Titanium and Iron by Magnetic Separation

Effect of oxidization on enrichment behavior of TiO2 in titanium-bearing slag

Effect of TiO2 on the Sintering Behavior of Low-Grade Vanadiferous Titanomagnetite Ore