Different Crystal Forms of ZnS Nanomaterials for the Adsorption of Elemental Mercury

Yang Yang,Rui Huang,Wenqing Xu,Jixiang Zhang,Chaoqun Li,Jianfei Song,Tingyu Zhu

DOI: https://doi.org/10.1021/acs.est.0c05878

2021-02-06

Abstract:ZnS is a promising sorbent in recovering Hg⁰ from industrial flue gas due to its excellent Hg⁰ adsorption capacity. However, the internal structure–activity relationship still needs to be further clarified. In this work, ZnS sorbents with different structures were synthesized with the hydrothermal method by tuning the temperature. The samples had significant differences in the crystallinity, morphology, particle size, and sulfur (S) active sites. The results indicated that Hg⁰ removal performance was determined by the specific surface area and S active sites. ZnS synthesized at low temperatures (80-ZnS and 120-ZnS) had a larger surface area, while the S sites on the high-temperature-synthesized sample (160-ZnS) were more active for Hg⁰ adsorption. The 160-ZnS sample exhibited a much higher Hg⁰ adsorption amount per unit surface area. Further characterization revealed that S₂^2– and S<i>_x</i> were the main active sites for Hg⁰ adsorption. S<i>_x</i> existed in the form of long-chain polysulfur (L-S<i>_x</i>) on 80-ZnS and 120-ZnS, while it exhibited in the form of short-chain polysulfur (S-S<i>_x</i>) on 160-ZnS. L-S<i>_x</i> had negligible adsorption ability, while S-S<i>_x</i> had a high affinity for Hg⁰. Hg⁰ can react with S₂^2– and S-S<i>_x</i>, forming α-HgS and β-HgS, respectively. The new insight in this work can provide theoretical guidance for the design and structure optimization of ZnS, facilitating its practical industrial application.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.est.0c05878?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.est.0c05878</a>.Additional experimental data of sample characterization (Figures S1, S3, and S4); schematic diagram of the fixed-bed experimental system (Figure S2); breakthrough profile of 80-ZnS for long-time adsorption (Figure S5); influence of flue gas components on 80-ZnS (Figure S6); Hg-TPD peak fitting (Figure S7); comparison of 80-ZnS with other adsorbents for Hg⁰ capture (Table S1); summary of the active sites and corresponding products from the references (Table S2) (<a class="ext-link" href="/doi/suppl/10.1021/acs.est.0c05878/suppl_file/es0c05878_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

environmental sciences,engineering, environmental