Analysis of 316L stainless steel pipe of lead–bismuth eutectic cooled thermo-hydraulic loop

V. Shankar Rao,Jun Lim,IL. Soon Hwang

DOI: https://doi.org/10.1016/j.anucene.2012.05.009

IF: 1.9

2012-10-01

Annals of Nuclear Energy

Abstract:AISI 316L stainless steel pipe, used in lead–bismuth eutectic (LBE) loop for integrated test of operability and safety (HELIOS) of proliferation-resistant environment-friendly accident-tolerant continual and economical reactor (PEACER) was investigated to evaluate its corrosion resistance properties. The dimension of the pipe is as follows: length 1m, outer diameter 7.65cm, and thickness 0.5cm. The flow rate of LBE through the pipe under natural circulation was between 0.1 and 0.2m/s with dissolved oxygen concentration of 10−6wt.%. The maximum and minimum operating temperature of the investigated pipe in HELIOS was 673K and 523K, respectively. The surface morphologies of the inner wall were examined using the field emission scanning electron microscope (FESEM) and cross-sectional analysis was carried out using the focused ion beam (FIB) technique. Energy dispersive X-ray (EDX) and X-ray diffraction (XRD) were employed for identification of the elements and their phases in scales. The surface of the inner wall of the pipe was covered with mixed layers of LBE, iron oxides and plumboferrite. Cross-sectional analysis revealed oxide scale consists of two layers, the inner layer composed of chromium and iron oxides, and the outer layer iron oxides and plumboferrite.

nuclear science & technology