Abstract:PURPOSE:To evaluate the effect of surface treatment on bonding strength between pure titanium formed by selective laser melting and porcelain.METHODS:Pure titanium strips (64) and cobalt-chromium alloy strips (16) were laser machined to meet ISO 9693 standards. The pure titanium specimens were divided into 4 groups according to the sandblasting pressure and interlayer material. The sandblasting pressure of 0.25 MPa of bonder porcelain group was TB1, the sandblasting pressure of 0.25 MPa of gold coating group was TG1, the sandblasting pressure of 0.45 MPa of bonder porcelain group was TB2, and the sandblasting pressure of 0.45 MPa of the gold coating group was TG2(n=16). After porcelain fusing, half of the specimens in each group were tested for three-point bend bonding strength, and the other half were tested after 10 000 cycles of thermal cycling(n=8). The bonding strength of cobalt-chromium alloy after sandblasting at 0.25 MPa and 0.45 MPa was taken as the control group and recorded as group C1, C2(n=8). The bonding strength was tested using classical three-point bending experiment. The surface roughness of pure titanium was measured by laser scanning confocal microscope(LSCM). Field emission scanning electron microscopy(FE-SEM) was used to observe the interface morphology of titanium-ceramic. The surface morphology of titanium after porcelain stripping was observed with stereomicroscope and fracture modes were analyzed by it. Graphpad Prism 8.0 software package was used for statistical analysis of the data.RESULTS:The bonding strength of group TG2 was (40.16±3.97) MPa and (37.38±2.39) MPa of group TG1, which were significantly higher than that of group TB2 (36.32±1.44) MPa and group TB1 (33.75±2.31) MPa (P＜0.05). The bonding strength of group TB2 with 0.45 MPa sandblasting was significantly higher than that of group TB1 with 0.25 MPa sandblasting (P＜0.05). There was no significant decrease in titanium-ceramic bonding strength before and after thermal cycling. When the sandblasting pressure increased from 0.25 MPa to 0.45 MPa, the roughness increased significantly (P＜0.05). The fracture modes were mixed.CONCLUSIONS:Under the conditions of this study, gold coating can significantly improve the bonding strength of Ti22 porcelain and SLM pure titanium than bonder porcelain, and increase of sandblasting pressure can further improve the bonding strength of titanium-porcelain. After 10 000 cycles of thermal cycling, the titanium-porcelain bonding strength did not decrease significantly.

Effect of surface porosity on ceramics during Al_2O_3/Ti bonding through brazing

Microstructure and Mechanical Properties of Ti6Al4V to Al2O3 Brazed Joints Using Ti-Ag/Cu-Ti Thin Films

Interface behavior of Al2O3/Ti joints produced by liquid state bonding

Effect of C/C Composite Surface Pretreatment on Properties of Brazed Joint

Enhanced bonding of Al2O3/Al2O3 joints brazed by Ni50Ti50 master alloy interlayer

Microstructure and Mechanical Properties of Al2O3/Cu Joints Brazed with Ag–Cu–Ti+Zn Composite Fillers

Secondary Phase Interaction at Interfaces of High-Strength Brazed Joints made using Liquid Phase Sintered Alumina Ceramics and Ag-Cu-Ti Braze Alloys

Brazing of C/C Composite and TiAl Alloy Using TiNiSi Filler Metal Added Cu Interlayer

Brazing between high purity alumina ceramics and titanium

Microstructure and mechanical properties of Al2O3 ceramic and copper joints brazed with AgCuInTi brazing alloy

Solid-Liquid State Bonding of Si3N4 Ceramics with Ceramic-Modified Brazing Alloy

The brazing of Al2O3 ceramic and other materials

Profiling interfacial reaction features and mechanical properties of B 4 C ceramic and Ti6Al4V titanium alloy brazed with Ag-based brazing filler

Effect of brazing process on microstructure evolution and mechanical properties of Ti6Al4V/ZrO2 joints after laser surface treatment

Effect of TiO2 addition on microstructure and mechanical properties of Al2O3 ceramic joints brazed with Ag‐CuO fillers

Brazing Between High Purity Alumina Ceramic and Oxygen-Free Copper

Compound connection mechanism of Al2O3 ceramic and TC4 Ti alloy with different joining modes

Effect of Surface Treatment on the Three-Point Bend Bonding Strength Between Pure Titanium Fabricated by Selec-Tive Laser Melting and Porcelain

Active Brazing of High Purity Alumina to Niobium Metal

Research of Alumina and Brazing Filler Metal Interface

Brazing Al2O3 to 4J42 Using Ag–Cu–Ti/Cu/BNi-2 Composite Fillers with Different Thicknesses of Cu Interlayer