Abstract:Purpose This study aims to evaluate the failure behavior of glass fiber-reinforced epoxy (GFRE) laminate subjected to cyclic loading conditions. It involves experimental investigation and statistical analysis using Weibull distribution to characterize the failure behavior of the GFRE composite laminate. Design/methodology/approach Fatigue tests were conducted using a tension–tension loading scheme at a frequency of 2 Hz and a loading ratio (R) of 0.1. The tests were performed at five different stress levels, corresponding to 50%–90% of the ultimate tensile strength (UTS). Failure behavior was assessed through cyclic stress-strain hysteresis plots, dynamic modulus behavior and scanning electron microscopy (SEM) analysis of fracture surfaces. Findings The study identified common modes of failure, including fiber pullouts, fiber breakage and matrix cracking. At low stress levels, fiber breakage, matrix cracking and fiber pullouts occurred due to high shear stresses at the fiber–matrix interface. Conversely, at high stress levels, fiber breakage and matrix cracking predominated. Higher stress levels led to larger stress-strain hysteresis loops, indicating increased energy dissipation during cyclic loading. High stress levels were associated with a more significant decrease in stiffness over time, implying a shorter fatigue life, while lower stress levels resulted in a gradual decline in stiffness, leading to extended fatigue life. Originality/value This study makes a valuable contribution to understanding fatigue behavior under tension–tension loading conditions, coupled with an in-depth analysis of the failure mechanism in GFRE composite laminate at different stress levels. The fatigue behavior is scrutinized through stress-strain hysteresis plots and dynamic modulus versus normalized cycles plots. Furthermore, the characterization of the failure mechanism is enhanced by using SEM imaging of fractured specimens. The Weibull distribution approach is used to obtain a reliable estimate of fatigue life.

Fatigue and post-fatigue static crack characterisation of a wrinkled thick glass fibre laminate in a composite wind turbine blade

A Hybrid Modeling Method of Fatigue Crack Growth for Gas Turbine Blades under Combined High and Low Cycle Fatigue Loadings

Static and fatigue cracking of thick carbon/glass hybrid composite laminates with complex wrinkle defects

Fatigue Crack Propagation Analysis in an Aero-Engine Turbine Disc Using Computational Methods and Spin Test

Full-Scale Fatigue Testing of a Wind Turbine Blade in Flapwise Direction and Examining the Effect of Crack Propagation on the Blade Performance

Fatigue life prediction for the main spar with wrinkle defects of a wind turbine blade

Damage Mode Identification of Composite Wind Turbine Blade under Accelerated Fatigue Loads Using Acoustic Emission and Machine Learning

Characterization of early fatigue damage in CFRP unidirectional laminates based on Micro‐CT

Analysis of Fatigue Cracking for Turbine Blade

Characterization and modeling of fatigue behavior of chopped glass fiber reinforced sheet molding compound (SMC) composite

Relationship between the Initial Fracture Stress and Fatigue Limit—Simple Prediction Method of Tensile Fatigue Limit of Composite

Formation mechanism and detection and evaluation methods as well as repair technology of crack damage in fiber-reinforced composite wind turbine blade: a review

Investigation of failure behavior of glass fiber reinforced epoxy laminate under fatigue loading

Integrating variable wind load, aerodynamic, and structural analyses towards accurate fatigue life prediction in composite wind turbine blades

Comparison of damage mechanisms in chopped strand mat and woven roving mat composites under cyclic tension

Fatigue behaviour of cracked steel plates reinforced with uhm cfrp laminate

Infusible thermoplastic composites for wind turbine blade manufacturing: fatigue life of thermoplastic laminates under ambient and low‐temperature conditions

Study of tensile‐tensile fatigue behavior of patch repaired carbon‐glass hybrid composite

State of the art in fatigue modelling of composite wind turbine blades

Characterization and Modelling of Multiple Intralaminar Cracking Initiation under Tensile Quasi-Static and Fatigue Loading

Progressive Fatigue Modelling of Open-Hole Glass-Fibre Epoxy Laminates