Infusible thermoplastic composites for wind turbine blade manufacturing: fatigue life of thermoplastic laminates under ambient and low‐temperature conditions

Dylan S. Cousins,Zach Arwood,Stephen Young,David Snowberg,Dayakar Penumadu,Aaron P. Stebner,Brandon Hinkel

DOI: https://doi.org/10.1002/adem.202201941

IF: 3.6

2023-03-01

Advanced Engineering Materials

Abstract:Traditionally, thermoset resins such as polyesters and epoxies have been used as the polymer matrix for construction of wind turbine blades. However, concern about their end‐of‐life treatment has garnered interest to use thermoplastics for increased recyclability. However, the high viscosity of molten thermoplastics inhibits their use in manufacturing wind turbine blades with injection or compression molding. A recently‐developed, infusible, reactive thermoplastic resin overcomes this technological barrier. Toward verifying that this recyclable resin is suitable for use in wind turbine blades, we provide a dataset of R = 0.1 and R = 10 fatigue data for glass fiber reinforced acrylic composites and demonstrate equal fatigue life to industry standard epoxy and unsaturated polyester resin systems. Specifically, we tabulate R = 0.1 fatigue data for acrylic composites at room temperature and ‐30 °C for verification of low‐temperature performance. To elucidate failure mechanisms, in situ mechanical testing with X‐ray computed tomography demonstrates that damage accumulation occurs by crack propagation along the fiber‐matrix interface under cyclic loading. IR thermography predicts failure points in composites specimens with porosity defects introduced from nonideal manufacturing processes. Furthermore, these manufacturing defects are shown to compromise the fatigue life of the acrylic laminates by an order of magnitude. This article is protected by copyright. All rights reserved.

materials science, multidisciplinary