Unlocking Room-Temperature Bistable Spin Transition at the Nanoscale: Synthesis of Core@Shell [Fe(NH2Trz)3(NO3)2]@SiO2 Nanoparticles

Alejandro Regueiro,Maria Marti-Carrascosa,Ramón Torres-Cavanillas,Eugenio Coronado

DOI: https://doi.org/10.1039/d4dt00911h

IF: 4

2024-05-01

Dalton Transactions

Abstract:In this work, we address the synthesis of stable spin-crossover nanoparticles capable of undergoing a hysteretic spin transition at room temperature. For this purpose we use the reverse micelle protocol to prepare naked [Fe(NH2Trz)3](NO3)2 and core@shell [Fe(NH2Trz)3](NO3)2@SiO2 nanoparticles. Through meticulous adjustment of synthetic parameters, we achieved nanoparticle sizes ranging from approximately 40 nm to 60 nm. Our findings highlight that [Fe(NH2Trz)3](NO3)2 presents a modest thermal hysteresis of 7 K, which decreases by the downsizing. Conversely, silica-coated nanoparticles with sizes of ca. 60 and 40 nm demonstrate a remarkable hysteretic response of approximately 30 K, switching their spin state around room temperature. Moreover, the presence of a SiO2 shell substantially enhances the nanoparticles' stability against oxidation. In this context, the larger 60 nm [Fe(NH2Trz)3](NO3)2@SiO2 hybrid remains stable in water for up to two hours, enabling the observation of an unreported water-induced spin transition after 30 min. Therefore, this work also introduces an intriguing avenue for inducing spin transitions through solvent exchange, underscoring the versatility and potential of these nanoparticles.

chemistry, inorganic & nuclear