Spin switching in electronic devices based on 2D assemblies of spin-crossover nanoparticles

Julien Dugay,Mónica Giménez-Marqués,Tatiana Kozlova,Henny W Zandbergen,Eugenio Coronado,Herre S. J. van der Zant

DOI: https://doi.org/10.48550/arXiv.1412.1345

2014-12-03

Abstract:In this communication we study the transport properties of two-dimensional assemblies of [Fe(Htrz)2(trz)](BF4) spin-crossover nanoparticles (NPs) with two different morphologies. The NPs have been synthesized made in a similar manner than in our previous study in which single NPs were measured. We prepared free-standing self-assembled monolayer sheets of both SCO NPs formed at the air/liquid interface on holey carbon TEM grids to extract their global arrangement and NP size distributions by STEM-HAADF technique. The SCO NP systems present a rod-like shape and possess two different volumes, corresponding to lengths of 25 nm and 44 nm along the rod direction and average diameters of 10 nm and 6 nm respectively. In a similar manner, sheets of SCO NPs with the two different morphologies were electrically measured by contacting them on pre-patterned gold electrodes substrates. For both NP morphologies, a thermal hysteresis loop in the electrical conductance near room temperature was observed, which was correlated to their morphologies and 2D organization. The most remarkable result was the observation of an unprecedented large change in the electrical conductance of the two spin states, increasing by up to two orders of magnitude in the 2D assemblies of spin-crossover NPs. This value is significantly larger than that obtained in single-NP measurements (~ 3). Although such large conductance changes are not fully understood, our results point at important contributions from its size/morphology-dependence at the nanoscale.

Mesoscale and Nanoscale Physics

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore the spin - conversion characteristics of spin - crossover (SCO) nanoparticles based on two - dimensional assembly in electronic devices, especially to study the electrical transport properties of these nanoparticles in different morphologies and their relationship with the thermal hysteresis loop. Specifically, the paper focuses on the following aspects:

1. **Application potential of spin - conversion materials**: Spin - crossover materials can change their ground - state spin state (from low - spin LS to high - spin HS) under external physical or chemical stimuli, and this phenomenon is particularly significant near room temperature. Researchers have always hoped to apply this phenomenon to solid - state electronic devices, but previous studies have mostly focused on the micro - and meso - scales, and there are fewer studies on electrically - controlled spin - conversion on the nano - scale.

2. **Effect of nanoparticle morphology on electrical transport properties**: The paper studied two different morphologies of SCO nanoparticles (25/10 nm and 44/6 nm respectively) and explored how their morphologies affect the electrical transport properties and the shape of the thermal hysteresis loop. This helps to understand the spin - conversion mechanism at the nano - scale and provides a theoretical basis for designing high - performance nano - electronic devices.

3. **Relationship between spin state and electrical conductivity**: It was found that in nanoparticle assemblies, the high - spin state (HS) usually corresponds to a lower electrical conductivity, while in a single nanoparticle, the opposite is true. This difference suggests that there may be different transport mechanisms at different scales, and further research is needed to reveal the underlying physical mechanisms.

4. **Characteristics of the thermal hysteresis loop**: Through experimental measurements, the paper shows the characteristics of the thermal hysteresis loop of different morphologies of SCO nanoparticles in two - dimensional assemblies and explores the relationship between these characteristics and the nanoparticle morphology and assembly method. The research shows that longer nanorods (such as 44/6 nm) exhibit a wider thermal hysteresis loop and a higher transition temperature, which may be related to their stronger cooperative effect.

In summary, this paper aims to deeply understand the electrical transport behavior of spin - crossover nanoparticles in two - dimensional assemblies, especially the characteristics of the thermal hysteresis loop in different morphologies, so as to provide scientific basis and technical support for the development of new spintronic devices.